'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PC LEXAN™ CFR7630-GY2G079T SABIC INNOVATIVE NANSHA
99
- Unit Price:US$ 9,394 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:Non chloro non bromine flame retardant
- Application Areas:Electronic and Electrical Applications｜Plastic bag｜Lighting applications｜Electrical appliances
- Color:--
- Grade:--
Technical Data Sheet
| optical performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| transmissivity | 2000μm | Internal Method | >89.0 | % |
| 1000μm | Internal Method | >90.0 | % | |
| 3000μm | Internal Method | >88.0 | % | |
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 66.0 | J |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NoBreak | |
| -30°C | ISO 180/1U | NoBreak | ||
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 10 | kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 9.0 | kJ/m² |
| 23°C | ISO 179/1eA | 10 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak | |
| 23°C | ISO 179/1eU | NoBreak | ||
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 9.0 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| Extreme Oxygen Index | ISO 4589-2 | 45 | % | |
| Hot filament ignition temperature | 1.0mm | IEC 60695-2-13 | 875 | °C |
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 960 | °C |
| UL flame retardant rating | 3.0mm | UL 94 | 5VA | |
| 1.0mm | UL 94 | V-0 | ||
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Bending modulus | ISO 178 | 2500 | Mpa | |
| bending strength | ISO 178 | 103 | Mpa | |
| Yield,50.0mmSpan | ASTM D790 | 106 | Mpa | |
| Tensile modulus | ASTM D638 | 2500 | Mpa | |
| ISO 527-2/1 | 2400 | Mpa | ||
| tensile strength | Yield | ASTM D638 | 68.0 | Mpa |
| Yield | ISO 527-2/50 | 67.0 | Mpa | |
| Break | ASTM D638 | 52.0 | Mpa | |
| Break | ISO 527-2/50 | 52.0 | Mpa | |
| elongation | Yield | ASTM D638 | 6.0 | % |
| Tensile strain | Yield | ISO 527-2/50 | 6.0 | % |
| elongation | Break | ASTM D638 | 51 | % |
| Tensile strain | Break | ISO 527-2/50 | 23 | % |
| Bending modulus | 50.0mmSpan | ASTM D790 | 2400 | Mpa |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTM D648 | 120 | °C |
| 1.8MPa,Unannealed,100mmSpan | ISO 75-2/Ae | 120 | °C | |
| 0.45MPa,Unannealed,100mmSpan | ISO 75-2/Be | 131 | °C | |
| 0.45MPa,Unannealed,3.20mm | ASTM D648 | 131 | °C | |
| RTI Str | UL 746 | 125 | °C | |
| Vicat softening temperature | ASTM D152510 | 136 | °C | |
| -- | ISO 306/B50 | 137 | °C | |
| -- | ISO 306/B120 | 139 | °C | |
| Ball Pressure Test | 125°C | IEC 60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 6.6E-05 | cm/cm/°C |
| MD：23to80°C | ISO 11359-2 | 7.2E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 7E-05 | cm/cm/°C | |
| TD：23to80°C | ISO 11359-2 | 7.6E-05 | cm/cm/°C | |
| RTI Elec | UL 746 | 125 | °C | |
| RTI Imp | UL 746 | 120 | °C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Outdoor applicability | UL 746C | f1 | ||
| Water absorption rate | Equilibrium,23°C,50%RH | ISO 62 | 0.11 | % |
| Saturation,23°C | ISO 62 | 0.14 | % | |
| Shrinkage rate | TD：3.20mm | Internal Method | 0.60-0.80 | % |
| MD：3.20mm | Internal Method | 0.55-0.75 | % | |
| Melt Volume Flow Rate (MVR) | 300°C/1.2kg | ISO 1133 | 5.00 | cm3/10min |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 5.0 | g/10min |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Dissipation factor | 1.10GHz | ASTMES7-83 | 5.8E-03 | |
| Dielectric constant | 1.10GHz | ASTMES7-83 | 2.79 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.