ABS POLYLAC® PA-765A J01 TAIWAN CHIMEI
337
- Unit Price:US$ 4,875 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:35MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜High mobility
- Application Areas:Fitness equipment｜Home appliance components｜Electronic field｜Electrical field
- Color:--
- Grade:--
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 101 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火 | ASTMD648 | 76.0 °C |
| 1.8MPa,退火 | ASTM D648 | 85.0 °C | |
| 1.8MPa,退火 | ISO 75-2/A | 84.0 °C | |
| vicat | -- | ASTM D15257 | 92.0 °C |
| -- | ISO 306/A50 | 93.0 °C | |
| -- | ISO 306/B50 | 79.0 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8.5E-05 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-1 |
| 2.5mm | UL 94 | V-0 | |
| 3.0mm | UL 94 | 5VA |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179 | 10 kJ/m² |
| 23°C | ISO 179 | 24 kJ/m² | |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 230 J/m |
| 23°C,6.40mm | ASTM D256 | 200 J/m | |
| -30°C | ISO 180/1A | 10 kJ/m² | |
| 23°C | ISO 180/1A | 23 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | --3 | ASTM D792 | 1.17 g/cm³ |
| 23°C | ISO 1183 | 1.17 g/cm³ | |
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 4.6 g/10min |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 46.0 cm3/10min |
| shrinkage rate | ISO 294-4 | 0.30-0.60 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 屈服4 | ASTM D638 | 39.1 Mpa |
| 屈服 | ISO 527-2/50 | 38.0 Mpa | |
| 断裂 | ISO 527-2/50 | 29.0 Mpa | |
| elongation | 断裂4 | ASTM D638 | 20 % |
| 断裂 | ISO 527-2/50 | 10 % | |
| flexural modulus | --5 | ASTM D790 | 2210 Mpa |
| --6 | ISO 178 | 1800 Mpa | |
| bending strength | --5 | ASTM D790 | 62.5 Mpa |
| --6 | ISO 178 | 56.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.