Material Properties:Glass fiber reinforced｜High impact resistance
Application Areas:household electrical appliances｜Electronic and electrical components
Color:--
Grade:Medical grade

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
transmissivity	Total,3000μm	ISO 13468	86.0	%
turbidity	3000μm	ISO 14782	3.0	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C,12.7mm	ASTM D256	170	J/m
Charpy Notched Impact Strength	23°C	ISO 179	14	kJ/m²
Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	180	J/m
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength		ASTM D638	43.0	Mpa
tensile strength	tensile strength	Yield,23°C	ISO 527-2	50.0	Mpa
elongation	Break	ASTM D638	20	%
Tensile strain	Break,23°C	ISO 527-2	14	%
Bending modulus		ASTM D790	2100	Mpa
Bending modulus	Bending modulus	23°C	ISO 178	2180	Mpa
bending strength		ASTM D790	67.0	Mpa
bending strength	bending strength	23°C	ISO 178	71.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	79.0	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	75.0	°C
Vicat softening temperature			80.0to85.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792	1.09	g/cm³
density	density	23°C	ISO 1183	1.09	g/cm³
melt mass-flow rate	220°C/10.0kg	ISO 1133	18	g/10min
Shrinkage rate		Internal Method	0.40-0.60	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Sale,23°C	ASTM D785	110
Rockwell hardness	Rockwell hardness	R-Sale,23°C	ISO 2039-2	110

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.