POM HOSTAFORM® M270NAT CELANESE USA

Unit Price:US$ 2,610 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Transaction Guarantee:

Supplier Information

Shanghai Huibao Material Technology Co., Ltd

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Low molecular weight｜Good forming performance｜High mobility
Application Areas:Household appliances｜Household appliances｜Automotive sector
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179/1eA	5.2	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	110	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	120	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	5.4	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Yield	ISO 527-2/1A/50	67.0	Mpa
Tensile strain	Yield	ISO 527-2/1A/50	8.0	%
Tensile creep modulus	1hr	ISO 899-1	2300	Mpa
Tensile creep modulus	Tensile creep modulus	1000hr	ISO 899-1	1300	Mpa
Bending modulus	23°C	ISO 178	2750	Mpa
Tensile modulus		ISO 527-2/1A/1	2800	Mpa
tensile strength	Yield,23°C	ASTM D638	60.7	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	110	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	103	°C
Melting temperature		ISO 11357-3	166	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	1.1E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	1.2E-04	cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	156	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Density of Melt		Internal Method	1.200	g/cm³
SpecificHeatCapacity of Melt		Internal Method	2210	J/kg/°C
ThermalConductivityofMelt		Internal Method	0.16	W/m/K
density		ISO 1183	1.41	g/cm³
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	23.0	cm3/10min
Shrinkage rate	MD	ASTM D955	2.2	%
	Shrinkage rate	TD	ASTM D955	1.8	%
		Shrinkage rate	TD	ISO 294-4	1.6	%
		Shrinkage rate	Shrinkage rate	MD	ISO 294-4	1.7	%
Water absorption rate	Saturation,23°C	ISO 62	0.75	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.20	%
density		ASTM D792	1.41	g/cm³

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Dongguan Yiwei Plastic	US$ 2350 /MT
ASIAPLAS	US$ 2610 /MT

Supplier Join

Get App

Top

POM HOSTAFORM® M270NAT CELANESE USA

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index