Material Properties:Low temperature impact resistance｜Resistance to stress cracking｜Fatigue resistance
Application Areas:Automotive Applications
Color:--
Grade:--

Technical Data Sheet Compare

thermal performance	Test Condition	Test Method	Test Result
vicat		ISO 306/A	150 °C
vicat	vicat		ISO 306/B	155 °C
melting temperature		ISO 11357	178 °C
Heat Deflection Temperature		ISO 75-2/B	150 °C
Heat Deflection Temperature	Heat Deflection Temperature		ISO 75-2/A	55.0 °C
Linear coefficient of thermal expansion		ISO 11359-2	1.3E-04 cm/cm/°C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB
UL flame retardant rating	UL flame retardant rating		UL 94	HB

Mechanical properties	Test Method	Test Result
Nominal tensile fracture strain	ISO 527-2	>50 %
Tensile strain	ISO 527-2	5.0 %
Tensile modulus	ISO 527-2	2000 Mpa
tensile strength	ISO 527-2	47.0 Mpa

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO 179/1eA	6.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO 179/1eA	6.0 kJ/m²
Impact strength of simply supported beam without notch		ISO 179/1eU	160 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch		ISO 179/1eU	160 kJ/m²

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate		ISO 62	1.1 %
Water absorption rate	Water absorption rate		ISO 62	0.50 %
shrinkage rate		ISO 294-4	1.2 %
shrinkage rate	shrinkage rate		ISO 294-4	1.2 %
density		ISO 1183	1.25 g/cm³

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.