Material Description
- Material Properties:heat-resisting｜Low shrinkage｜Dimensional stability｜Low viscosity｜High temperature strength｜Weldable｜Aging resistance｜Antichemical
- Application Areas:fibre
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R 级 | ASTM D785 | 91 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8 MPa, 未退火 | ASTM D648 | 310 °C |
| Linear coefficient of thermal expansion | 流动 : 150°C | 内部方法 | 2.0E-6 cm/cm/°C |
| 横向 : 150°C | 内部方法 | 8.1E-5 cm/cm/°C | |
| thermal conductivity | JIS R2618 | 0.53 W/m/K |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.30 mm | UL 94 | V-0 |
| Limiting Oxygen Index | ISO 527-1 | 44 % | |
| Solder resistance | 内部方法 | 335 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 6.40 mm | ASTM D256 | 460 J/m |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | 横向流量 | 内部方法 | 0.78 % |
| 流量 | 内部方法 | 0.11 % | |
| Water absorption rate | 饱和 | ASTM D570 | 0.020 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | ASTM D257 | 1.0E+15 ohms·cm | |
| dielectric constant | 1 kHz | ASTM D150 | 4.40 |
| 1 MHz | ASTM D150 | 3.70 | |
| Dissipation Factor | 1 kHz | ASTM D150 | 0.018 |
| 1 MHz | ASTM D150 | 0.035 | |
| arc resistance | ASTM D495 | 130 sec | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 130 °C | ||
| drying time | 4.0 to 24 hr | ||
| Temperature at the rear of the barrel | 330 to 350 °C | ||
| Temperature in the middle of the barrel | 350 to 370 °C | ||
| Temperature at the front of the material cylinder | 370 to 390 °C | ||
| Spray nozzle temperature | 370 to 390 °C | ||
| Processing (melt) temperature | 380 °C | ||
| mold temperature | 40 to 160 °C | ||
| Injection Pressure | 120 to 160 Mpa | ||
| injection speed | 中等偏快 | ||
| pressure holding | 40.0 to 60.0 Mpa | ||
| Back pressure | 1.00 to 5.00 Mpa | ||
| screw speed | 50 to 100 rpm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D638 | 182 Mpa | |
| elongation | 断裂 | ASTM D638 | 5.6 % |
| flexural modulus | 23°C | ASTM D790 | 11900 Mpa |
| 200°C | ASTM D790 | 5780 Mpa | |
| bending strength | 23°C | ASTM D790 | 155 Mpa |
| 200°C | ASTM D790 | 47.0 Mpa | |
| shear strength | ASTM D732 | 58.0 Mpa | |
| Poisson's ratio | ASTM D785 | 0.48 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.