PBT

PBT VALOX™ ENH4550-1001 SABIC INNOVATIVE SHANGHAI

242

Unit Price:US$ 4,537 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
33MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High rigidity｜high strength
Application Areas:Home appliance components｜Automotive Applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C,TotalEnergy	ASTM D3763	6.50 J
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	33 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	29 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	7.0 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/2U	33 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/2U	36 kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	7.0 kJ/m²

flammability	Test Condition	Test Method	Test Result
Burning wire flammability index	0.75mm	IEC 60695-2-12	960 °C
UL flame retardant rating	3.0mm	UL 94	5VA
UL flame retardant rating	UL flame retardant rating	0.75mm	UL 94	V-0
Hot filament ignition temperature	0.8mm	IEC 60695-2-13	775 °C
Hot filament ignition temperature	Hot filament ignition temperature	3.0mm15	IEC 60695-2-13	775 °C

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield	ASTM D638	105 Mpa
Tensile modulus		ISO 527-2/1	10400 Mpa
Tensile modulus	Tensile modulus		ASTM D638	9900 Mpa
tensile strength	Yield	ISO 527-2/5	112 Mpa
	tensile strength	Break	ASTM D638	105 Mpa
	tensile strength	tensile strength	Break	ISO 527-2/5	112 Mpa
elongation	Yield	ASTM D638	2.0 %
Tensile strain	Yield	ISO 527-2/5	2.0 %
elongation	Break	ASTM D638	2.0 %
Tensile strain	Break	ISO 527-2/5	2.0 %
Bending modulus	50.0mmSpan	ASTM D790	9100 Mpa
Bending modulus	Bending modulus		ISO 178	9400 Mpa
bending strength		ISO 178	170 Mpa
bending strength	bending strength	Yield,50.0mmSpan	ASTM D790	161 Mpa
Fracture bending strain		ISO 178	2.0 %

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	216 °C
	Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	219 °C
		Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	204 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	201 °C
Linear coefficient of thermal expansion	TD：-40to150°C	ASTME831	7.7E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	7.1E-05 cm/cm/°C
Vicat softening temperature	--	ASTM D152513	202 °C
	Vicat softening temperature	--	ISO 306/B120	206 °C
		Vicat softening temperature	--	ISO 306/A50	219 °C
		Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	206 °C
Ball Pressure Test	125°C	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	2.7E-05 cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to150°C	ASTME831	2.2E-05 cm/cm/°C
		Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	3E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23to80°C	ISO 11359-2	2.2E-05 cm/cm/°C
Vicat softening temperature	--	ASTM D152512	215 °C
RTI Str		UL 746	140 °C
RTI Imp		UL 746	140 °C
RTI Elec		UL 746	130 °C
Linear coefficient of thermal expansion	TD：23to80°C	ISO 11359-2	9.1E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	7.6E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.060 %
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.23 %
Shrinkage rate	TD：3.20mm	Internal Method	0.50-1.1 %
	Shrinkage rate	TD：--2	Internal Method	0.60-1.2 %
		Shrinkage rate	MD：3.20mm	Internal Method	0.10-0.50 %
		Shrinkage rate	Shrinkage rate	MD：--2	Internal Method	0.10-0.50 %
Melt Volume Flow Rate (MVR)	250°C/5.0kg	ISO 1133	20.0 cm3/10min
melt mass-flow rate	250°C/5.0kg	ASTM D1238	27 g/10min
MeltViscosity	250°C,1500sec^-1	ISO 11443	210 Pa·s

Electrical performance	Test Condition	Test Method	Test Result
Hot wire ignition	HWI	UL 746	PLC 0
High voltage arc tracing rate	HVTR	UL 746	PLC 0
High arc combustion index	HAI	UL 746	PLC 0
Compared to the anti leakage trace index		IEC 60112	V
Compared to the anti leakage trace index	Compared to the anti leakage trace index	CTI	UL 746	PLC 2
Arc resistance		ASTM D495	PLC6
Dielectric strength	3.20mm,in Oil	ASTM D149	21 KV/mm
Dielectric strength	Dielectric strength	3.20mm,inAir	ASTM D149	21 KV/mm
Volume resistivity		IEC 60093	1.0E+15to1.0E+16 ohms·cm
Volume resistivity	Volume resistivity		ASTM D257	1.0E+15to1.0E+16 ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PBT VALOX™ ENH4550-1001 SABIC INNOVATIVE SHANGHAI

Material Description

Technical Data Sheet Compare

Technical Data Sheet