Material Description
- Material Properties:Filler: Glass fiber reinforced material｜25% filler by weight
- Application Areas:--
- Color:--
- Grade:Flame retardant enhanced grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | ISO 75-2/B | 240 °C | |
| ISO 75-2/A | 220 °C | ||
| vicat | ISO 306/B50 | 235 °C | |
| melting temperature | ISO 11357-3 | 262 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | FMVSS 302 | < 100 mm/min | |
| UL flame retardant rating | UL 94 | V-0 | |
| Burning wire flammability index | IEC 60695-2-12 | 960 °C | |
| Hot filament ignition temperature | IEC 60695-2-13 | 775 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 8000 Mpa | |
| tensile strength | ISO 527-2/5 | 110 Mpa | |
| Tensile strain | ISO 527-2/5 | 2.5 % | |
| flexural modulus | ISO 178 | 7000 Mpa | |
| bending strength | ISO 178 | 170 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 5.5 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179/1eU | 35 kJ/m² | |
| Impact strength of cantilever beam gap | ISO 180/1A | 5.5 kJ/m² | |
| Suspended wall beam without notch impact strength | ISO 180/1U | 30 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.39 g/cm³ |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1.0E+13 ohms | |
| volume resistivity | IEC 60093 | 1.0E+15 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 75 to 85 °C | ||
| drying time | 2.0 to 4.0 hr | ||
| Processing (melt) temperature | 270 to 290 °C | ||
| mold temperature | 80 to 100 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.