PA66 Zytel® FG133F1 NC010 DUPONT USA
151
- Unit Price:US$ 3,286 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:21.3MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Non enhanced
- Application Areas:Non specific food
- Color:--
- Grade:--
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8 MPa, 未退火 | ISO 75-2/A | 78.0 °C |
| melting temperature | ISO 11357-3 | 262 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | 1.00 mm | ISO 3795 | < 100 mm/min |
| FMVSS combustion rate | FMVSS 302 | B |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Ejection Temperature | 190 °C |
| squeeze out | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 80 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.060 % | ||
| Melt Temperature | 235 to 250 °C | ||
| Extrusion Melt Temperature, Optimum | 240 °C |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | 横向流量 | ISO 294-4 | 1.0 % |
| 流量 | ISO 294-4 | 0.80 % |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 80 °C | ||
| Drying time - hot air dryer | 2.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.20 % | ||
| Processing (melt) temperature | 280 to 300 °C | ||
| Melt Temperature, Optimum | 290 °C | ||
| mold temperature | 50 to 90 °C | ||
| Mold Temperature, Optimum | 70 °C | ||
| pressure holding | 50.0 to 100 Mpa | ||
| Drying Recommended | yes | ||
| Hold Pressure Time | 4.00 s/mm | ||
| Maximum Screw Tangential Speed | 24 m/min |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 3800 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 94.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2 | 6.0 % |
| Nominal tensile fracture strain | ISO 527-2 | 14 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.