EAA

EAA PRIMACOR™ 3330 STYRON US

464

Unit Price:US$ 3,414 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Heat sealing performance｜High toughness
Application Areas:Food service sector
Color:--
Grade:Extrusion grade

Technical Data Sheet

Other performance	Test Condition	Test Method	Test Result
Starting temperature of heat sealing		Internal Method	92.8 ℃
Water vapor permeability	38℃，90% RH	DIN 53122/2	g·mm/m

Basic Performance	Test Condition	Test Method	Test Result
Monomer content		Internal Method	%

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield,Compression Molded	ASTM D-638	8.34 MPa
	tensile strength	Yield,Compression Molded	ISO 527-2	8.34 MPa
		tensile strength	Compression Molded，Break	ASTM D-638	17.4 MPa
			tensile strength	Yield,Compression Molded	ASTMD638	8.34 Mpa
			tensile strength	tensile strength	Break,Compression Molded	ASTMD638	17.4 Mpa
elongation	Break,Compression Molded	ASTMD638	520 %
tensile strength	Compression Molded，Break	ISO 527-2	17.4 MPa
Elongation at Break	Compression Molded	ASTM D-638	520 %
Elongation at Break	Elongation at Break	Compression Molded	ISO 527-2	520 %

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature		ASTMD1525	85.0 °C
Melting temperature		Internal Method	100 °C
Vicat softening temperature		ASTM D-1525	85 ℃
Vicat softening temperature	Vicat softening temperature		ISO 306	85 ℃

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	190°C/2.16kg	ASTMD1238	5.8 g/10min
Content of comonomer		Internal Method	6.5 %

film	Test Condition	Test Method	Test Result
Initial sealing temperature		Internal Method	92.8 °C
Water vapor permeability	38°C,90%RH	DIN 53122/2	0.40 g·mm/m²/atm/24hr

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

EAA PRIMACOR™ 3330 STYRON US

Material Description

Technical Data Sheet Compare

Technical Data Sheet