PC LEXAN™  3412ECR GY1D640L SABIC INNOVATIVE NANSHA

181
  • Unit Price:US$ 2,302 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    20MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Glass fiber reinforced｜enhance｜Flame retardant｜High rigidity
  • Application Areas:Plastic bag｜Automotive External Parts｜Industrial applications｜Electrical appliances｜Lighting applications｜Medical supplies
  • Color:--
  • Grade:Light diffusion level

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Suspended wall beam without notch impact strength23°CISO 180/1U35 kJ/m²
Dart impact23°C,TotalEnergyASTM D376320.0 J
Impact strength of cantilever beam gap23°CASTM D256110 J/m
Impact strength of cantilever beam gap-30°CISO 180/1A6.0 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A7.0 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1U35 kJ/m²
Impact strength of cantilever beam gap-30°CASTM D256110 J/m
Impact strength of simply supported beam without notch23°CISO 179/1eU40 kJ/m²
Charpy Notched Impact Strength-30°CISO 179/1eA5.0 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA6.0 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU40 kJ/m²
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating1.5mmUL 94V-0
UL flame retardant rating3.0mmUL 945VA
Burning wire flammability index1.0mmIEC 60695-2-12960 °C
Hot filament ignition temperature1.0mmIEC 60695-2-13825 °C
Extreme Oxygen IndexISO 4589-240 %
mechanical propertiesTest ConditionTest MethodTest Result
tensile strengthBreakISO 527-2/590.0 Mpa
tensile strengthBreakASTM D63887.0 Mpa
tensile strengthYieldISO 527-2/595.0 Mpa
tensile strengthYieldASTM D63890.0 Mpa
Tensile modulusISO 527-2/16000 Mpa
Tensile modulusASTM D6385500 Mpa
elongationYieldASTM D6383.1 %
Tensile strainYieldISO 527-2/52.8 %
Tensile strainBreakISO 527-2/53.2 %
Bending modulus50.0mmSpanASTM D7905000 Mpa
Bending modulusISO 1785500 Mpa
bending strengthISO 178140 Mpa
bending strengthYield,50.0mmSpanASTM D790156 Mpa
thermal performanceTest ConditionTest MethodTest Result
RTI ImpUL 746130 °C
RTI ElecUL 746130 °C
Linear coefficient of thermal expansionTD：23to80°CISO 11359-27E-05 cm/cm/°C
Linear coefficient of thermal expansionMD：-40to40°CASTME8313E-05 cm/cm/°C
Ball Pressure Test125°CIEC 60695-10-2Pass
Vicat softening temperature--ISO 306/B120146 °C
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af136 °C
Linear coefficient of thermal expansionTD：-40to40°CASTME8317E-05 cm/cm/°C
Linear coefficient of thermal expansionMD：23to80°CISO 11359-23E-05 cm/cm/°C
Vicat softening temperature--ISO 306/B50145 °C
Vicat softening temperatureASTM D152510147 °C
RTI StrUL 746130 °C
Hot deformation temperature0.45MPa,Unannealed,64.0mmSpanISO 75-2/Bf141 °C
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D648141 °C
Physical propertiesTest ConditionTest MethodTest Result
Water absorption rateEquilibrium,23°C,50%RHISO 620.12 %
Water absorption rateSaturation,23°CISO 620.29 %
Shrinkage rateTD：3.20mmInternal Method0.20-0.50 %
Shrinkage rateMD：3.20mmInternal Method0.20-0.50 %
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 11337.00 cm3/10min
melt mass-flow rate300°C/1.2kgASTM D12387.0 g/10min
densityISO 11831.36 g/cm³
densityASTM D7921.30 g/cm³
Electrical performanceTest ConditionTest MethodTest Result
Surface resistivityIEC 60093>1.0E+15 ohms
Volume resistivityIEC 60093>1.0E+15 ohms·cm
Relative permittivity50HzIEC 602503.30
Relative permittivity60HzIEC 602503.30
Relative permittivity1MHzIEC 602503.30
Dissipation factor50HzIEC 602500.020
Dissipation factor60HzIEC 602500.020
Dissipation factor1MHzIEC 602500.010
Arc resistanceASTM D495PLC7
Compared to the anti leakage trace indexCTIUL 746PLC 3
High arc combustion indexHAIUL 746PLC 3
High voltage arc tracing rateHVTRUL 746PLC 3
Hot wire ignitionHWIUL 746PLC 0
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.