GPPS POLYREX® PG-33 ZHENJIANG CHIMEI

Unit Price:US$ 1,680 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
19MT
Delivery Terms:
FOB
Port of Loading :
Lianyungang port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details
Material Comparison:
GPPS POLYREX® PG-33 TAIWAN CHIMEI

Transaction Guarantee:

Supplier Information

Dongguan Zhangmutou Runfeng Plastic Raw Material Business Department

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜transparent
Application Areas:Casters｜container｜Household goods｜Food containers｜Lampshade｜Audiotape
Color:--
Grade:Injection grade

Material Certification

MSDS

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	17	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,6.40mm	ASTM D256	15	J/m
Charpy Notched Impact Strength	23°C	ISO 179	2.7	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179	1.8	kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	1.8	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	4.0	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	75.0	Mpa
bending strength	bending strength		ASTM D790	65.6	Mpa
Bending modulus		ISO 178	3100	Mpa
Bending modulus	Bending modulus		ASTM D790	3030	Mpa
Tensile strain	Break	ISO 527-2/50	2.0	%
elongation	Break	ASTM D638	2.0	%
tensile strength	Break	ISO 527-2/50	48.0	Mpa
tensile strength	tensile strength	Break	ASTM D638	45.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	MD	ISO 11359-2	5.0E-5to8.0E-5	cm/cm/°C
Vicat softening temperature	--	ISO 306/B50	90.0	°C
	Vicat softening temperature	--	ISO 306/A50	94.0	°C
	Vicat softening temperature	Vicat softening temperature		ASTM D15257	94.0	°C
Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	87.0	°C
	Hot deformation temperature	1.8MPa,Annealed	ASTM D648	87.0	°C
		Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	76.0	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	79.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Melt Volume Flow Rate (MVR)	200°C/5.0kg	ISO 1133	8.00	cm3/10min
melt mass-flow rate	200°C/5.0kg	ASTM D1238	8.0	g/10min
density	23°C	ISO 1183	1.04	g/cm³
density	density	比重	ASTM D792	1.05	g/cm³
Shrinkage rate		ISO 294-4	0.40-0.70	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Scale	ASTM D785	77

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Shantou Qiheng Trading	US$ 1680 /MT
Guangdong Mingxin	US$ 1680 /MT
Jiangsu leads the way	US$ 1680 /MT
Dongguan Hongyunhui	US$ 1680 /MT
Guangdong Sinan	US$ 1680 /MT

Supplier Join

Get App

Top

GPPS POLYREX® PG-33 ZHENJIANG CHIMEI

Material Description

Material Certification

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index