impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C,6.40mm	ASTM D256	51	J/m
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.71mm	UL 94	HB
	UL flame retardant rating	1.5mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	3.3mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus	3.20mm	ASTM D790	1860	Mpa
bending strength	Yield,3.20mm	ASTM D790	65.7	Mpa
tensile strength	Yield,3.20mm	ASTM D638	46.1	Mpa
elongation	Break,3.20mm	ASTM D638	>100	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	57.0	°C
RTI		UL 746	140	°C
RTI Imp		UL 746	130	°C
Melting temperature		ASTM D3418	223	°C
RTI Elec		UL 746	140	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	23°C,24hr	ASTM D570	0.080	%
Shrinkage rate	MD	ASTM D955	1.2-2.0	%
melt mass-flow rate	250°C/2.16kg	ASTM D1238	34	g/10min
density		ASTM D792	1.29	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric strength	1.00mm	ASTM D149	23	KV/mm
Arc resistance		ASTM D495	PLC 5
Compared to the anti leakage trace index	CTI)5	UL 746	PLC 0
Compared to the anti leakage trace index	Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 0
Volume resistivity		ASTM D257	1E+17	ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.