Material Properties:Thermal stability｜High impact resistance
Application Areas:Power tool accessories｜Automotive components｜Home appliance components
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result
Melt volume flow rate		ISO 1133	39.0 cm3/10min
Shrinkage rate		ISO 294-4	1.7 %
Shrinkage rate	Shrinkage rate		ISO 294-4	1.9 %
Water absorption rate		ISO 62	0.60 %
melt mass-flow rate		ISO 1133	46 g/10min

hardness	Test Condition	Test Method	Test Result
Rockwell hardness		ISO 2039-2	80

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB

Supplementary Information	Test Condition	Test Method	Test Result
ColorNumber			CF2001

Mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	2600 Mpa
tensile strength		ISO 527-2	54.0 Mpa
Nominal tensile fracture strain		ISO 527-2	35 %
Flexural modulus		ISO 178	2400 Mpa
bending strength		ISO 178	79.0 Mpa
coefficient of friction		JISK7218	0.21
coefficient of friction	coefficient of friction		JISK7218	0.17
Wear factor		JISK7218	<1.0 10^-8mm³/N·m
	Wear factor		JISK7218	21 10^-8mm³/N·m
		Wear factor		JISK7218	80 10^-8mm³/N·m
		Wear factor	Wear factor		JISK7218	220 10^-8mm³/N·m

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ISO 75-2/A	98.0 °C
Linear coefficient of thermal expansion		内部方法	1.2E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		内部方法	1.2E-04 cm/cm/°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.