PC/PBT XENOY™ 5720U-1001 SABIC INNOVATIVE US
315
- Unit Price:US$ 2,897 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:133MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Chemical resistance｜Low temperature impact resistance
- Application Areas:Plastic bag｜Lighting applications｜Household daily necessities
- Color:--
- Grade:Cold resistant grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 108 °C |
| 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 117 °C | |
| 0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距12 | ISO 75-2/Bf | 109 °C | |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 83.0 °C | |
| 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 95.0 °C | |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距12 | ISO 75-2/Af | 87.0 °C | |
| vicat | -- | ASTM D152513 | 119 °C |
| -- | ISO 306/B120 | 122 °C | |
| Linear coefficient of thermal expansion | 流动 : -40 到 95°C | ASTM E831 | 9.8E-5 cm/cm/°C |
| 流动 : -30 到 80°C | ISO 11359-2 | 9.8E-5 cm/cm/°C | |
| 横向 : -40 到 95°C | ASTM E831 | 1.0E-4 cm/cm/°C | |
| 横向 : -30 到 80°C | ISO 11359-2 | 1.0E-4 cm/cm/°C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 47 kJ/m² |
| 23°C | ISO 179/1eA | 55 kJ/m² | |
| Dart impact | -40°C, Energy at Peak | ASTM D3763 | 49.0 J |
| -40°C, Total Energy | ASTM D3763 | 59.0 J | |
| -30°C, Energy at Peak | ASTM D3763 | 49.0 J | |
| -30°C, Total Energy | ASTM D3763 | 61.0 J | |
| -20°C, Energy at Peak | ASTM D3763 | 41.0 J | |
| -20°C, Total Energy | ASTM D3763 | 53.0 J | |
| 23°C, Energy at Peak | ASTM D3763 | 44.0 J | |
| 23°C, Total Energy | ASTM D3763 | 54.0 J |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Specific volume | ASTM D792 | 0.850 cm³/g | |
| melt mass-flow rate | 250°C/2.16 kg | ASTM D1238 | 3.8 g/10 min |
| 250°C/5.0 kg | ASTM D1238 | 11 g/10 min | |
| 265°C/2.16 kg | ASTM D1238 | 6.0 g/10 min | |
| 266°C/5.0 kg | ASTM D1238 | 20 g/10 min | |
| 250°C/2.16 kg | ISO 1133 | 3.0 g/10 min | |
| Melt volume flow rate | 250°C/2.16 kg | ISO 1133 | 3.00 cm3/10min |
| 250°C/5.0 kg | ISO 1133 | 10.0 cm3/10min | |
| 265°C/2.16 kg | ISO 1133 | 6.00 cm3/10min | |
| 265°C/5.0 kg | ISO 1133 | 18.0 cm3/10min | |
| shrinkage rate | 3.20 mm，Flow | 内部方法 | 1.0 - 1.2 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.28 % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.080 % |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 110 °C | ||
| drying time | 4.0 to 6.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 50 to 80 % | ||
| Temperature at the rear of the barrel | 245 to 265 °C | ||
| Temperature in the middle of the barrel | 250 to 270 °C | ||
| Temperature at the front of the material cylinder | 255 to 275 °C | ||
| Spray nozzle temperature | 255 to 270 °C | ||
| Processing (melt) temperature | 260 to 275 °C | ||
| mold temperature | 65 to 90 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| screw speed | 50 to 80 rpm | ||
| Exhaust hole depth | 0.013 to 0.020 mm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | --2 | ASTM D638 | 1830 Mpa |
| --3 | 内部方法 | 1830 Mpa | |
| --4 | ASTM D638 | 1810 Mpa | |
| -- | ISO 527-2/1 | 1790 Mpa | |
| tensile strength | 屈服5 | ASTM D638 | 47.0 Mpa |
| 屈服6 | 内部方法 | 45.0 Mpa | |
| 屈服7 | ASTM D638 | 44.0 Mpa | |
| 屈服 | ISO 527-2/5 | 44.0 Mpa | |
| 屈服 | ISO 527-2/50 | 47.0 Mpa | |
| 断裂7 | ASTM D638 | 50.0 Mpa | |
| 断裂6 | 内部方法 | 47.0 Mpa | |
| 断裂5 | ASTM D638 | 48.0 Mpa | |
| 断裂 | ISO 527-2/5 | 43.0 Mpa | |
| elongation | 屈服7 | ASTM D638 | 4.6 % |
| 屈服6 | 内部方法 | 4.6 % | |
| 屈服5 | ASTM D638 | 4.0 % | |
| 屈服 | ISO 527-2/5 | 4.1 % | |
| 屈服 | ISO 527-2/50 | 4.6 % | |
| 断裂7 | ASTM D638 | 120 % | |
| 断裂6 | 内部方法 | 110 % | |
| 断裂5 | ASTM D638 | 120 % | |
| 断裂 | ISO 527-2/5 | 110 % | |
| 断裂 | ISO 527-2/50 | 120 % | |
| flexural modulus | 50.0 mm 跨距8 | ASTM D790 | 1660 Mpa |
| --9 | ISO 178 | 1860 Mpa | |
| bending strength | --9,10 | ISO 178 | 71.0 Mpa |
| 屈服, 50.0 mm 跨距8 | ASTM D790 | 70.0 Mpa | |
| 断裂, 50.0 mm 跨距8 | ASTM D790 | 69.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.