PA/MXD6

PA/MXD6 RENY™ NXG5945LS MITSUBISHI ENGINEERING JAPAN

371

Unit Price:US$ 8,791 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
26MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High rigidity｜High impact｜Filler: Glass fiber reinforced material｜45% filler by weight
Application Areas:Electronic and Electrical Applications｜Automotive sector
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179	90 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.6mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	349 Mpa
Bending modulus		ISO 178	14300 Mpa
Tensile strain	Break	ISO 527-2	2.0 %
tensile strength	Break	ISO 527-2	208 Mpa
Tensile modulus		ISO 527-2	16000 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD	ISO 11359-2	5.6E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	1.1E-05 cm/cm/°C
Melting temperature		ISO 11357-3	257 °C
Glass transition temperature		ISO 11357-2	87.0 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	232 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.73 %
Shrinkage rate			0.32 %
Melt Volume Flow Rate (MVR)	280°C/5.0kg	ISO 1133	8.50 cm3/10min
melt mass-flow rate	280°C/5.0kg	ISO 1133	13 g/10min

Electrical performance	Test Condition	Test Method	Test Result
Relative permittivity	100Hz	IEC 60250	4.20
Dissipation factor	1MHz	IEC 60250	6.7E-03
Dissipation factor	Dissipation factor	100Hz	IEC 60250	5.5E-03
Relative permittivity	1MHz	IEC 60250	4.10

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.