'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PPO FLEX NORYL™ PX9406P-7001 SABIC INNOVATIVE SHANGHAI
16
- Unit Price:US$ 3,840 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:20MT
- Delivery Terms:FOB
- Port of Loading :Shanghai port, China
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
- Material Comparison:
Transaction Guarantee:
Supplier Information
Dongguan Jiantou Plastic Co., Ltd
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant
- Application Areas:Electronic communication accessories｜Electronic communication accessories｜building materials｜Profile
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Filling analysis | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Melt viscosity | 280°C, 1500 sec^-1 | ISO 11443 | 278 | Pa·s |
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 9.0 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 0.40 mm | UL 94 | V-2 | |
| 0.75 mm | UL 94 | V-0 | ||
| 2.5 mm | UL 94 | 5VA | ||
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Bending modulus | --2 | ISO 178 | 2600 | Mpa |
| -- | ASTM D790 | 2350 | Mpa | |
| Tensile strain | Break | ISO 527-2/50 | 4.5 | % |
| Break | Internal Method | 85 | % | |
| tensile strength | Yield | ISO 527-2/50 | 73.0 | Mpa |
| Yield | Internal Method | 63.0 | Mpa | |
| bending strength | --2,3 | ISO 178 | 108 | Mpa |
| -- | ASTM D790 | 99.0 | Mpa | |
| injection | Test Condition | Test Method | Test Result | Test Unit |
| drying temperature | 105 to 110 | °C | ||
| drying time | 3.0 to 4.0 | hr | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Suggested injection volume | 30 to 70 | % | ||
| Temperature at the rear of the barrel | 245 to 295 | °C | ||
| Temperature in the middle of the barrel | 255 to 300 | °C | ||
| Temperature at the front of the material cylinder | 265 to 305 | °C | ||
| Back pressure | 0.300 to 0.700 | Mpa | ||
| Spray nozzle temperature | 275 to 305 | °C | ||
| Processing (melt) temperature | 275 to 305 | °C | ||
| Mold temperature | 70 to 100 | °C | ||
| Screw speed | 20 to 100 | rpm | ||
| Exhaust hole depth | 0.038 to 0.051 | mm | ||
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Linear coefficient of thermal expansion | Across Flow : -40°C | ISO 11359-2 | 7.6E-5 | cm/cm/°C |
| Vicat softening temperature | -- | ISO 306/A120 | 151 | °C |
| Hot deformation temperature | 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span5 | ISO 75-2/Af | 117 | °C |
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | ISO 11359-2 | 6.6E-5 | cm/cm/°C |
| Flow : -30 to 30°C | TMA | 7.0E-5 | cm/cm/°C | |
| Ball Pressure Test | 125°C | IEC 60695-10-2 | 通过 | |
| Vicat softening temperature | -- | ISO 306/B120 | 142 | °C |
| Hot deformation temperature | 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 125 | °C |
| 0.45 MPa, Unannealed, 6.40 mm | ASTM D648 | 136 | °C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Water absorption rate | 24 hr | ASTM D570 | 0.070 | % |
| Shrinkage rate | 3.20 mm，Flow | Internal Method | 0.50 - 0.70 | % |
| Melt Volume Flow Rate (MVR) | 300°C/5.0 kg | ISO 1133 | 23.0 | cm3/10min |
| 280°C/5.0 kg | ISO 1133 | 10.0 | cm3/10min | |
| 280°C/10.0 kg | ISO 1133 | 27.0 | cm3/10min | |
| melt mass-flow rate | 250°C/10.0 kg | ASTM D1238 | 3.9 | g/10 min |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Surface resistivity | ASTM D257 | 1.0E+16 | ohms | |
| Dielectric constant | 60 Hz | ASTM D150 | 2.80 | |
| 50 kHz | ASTM D150 | 2.80 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.