TPV Santoprene™ 8191-60B500 CELANESE USA
222
- Unit Price:US$ 3,995 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:Chemical resistance|Flame retardant
- Application Areas:Profile|building materials|Kitchen utensils|Parts under the hood of a car|Movable hinge|Mirror frame|Adhesive resin|Soft handle|Consumer product application field|Fatigue relief supplies|Phone|Bonding|Application in the automotive field|sporting goods|Large and small household appliances|Home appliance components|packing|Electrical appliances
- Color:--
- Grade:Injection grade
Technical Data Sheet
flammability | Test Condition | Test Method | Test Result |
---|---|---|---|
UL flame retardant rating | 1.1mm | UL 94 | HB |
3.0mm | UL 94 | HB |
elastomer | Test Condition | Test Method | Test Result |
---|---|---|---|
elongation | Break,23°C,Across Flow | ASTM D412 | 600 % |
Break,23°C,Across Flow | ISO 37 | 600 % | |
Permanent compression deformation | 125°C,70hr | ASTM D395B | 55 % |
125°C,70hr | ISO 815 | 55 % |
hardness | Test Condition | Test Method | Test Result |
---|---|---|---|
Shore hardness | ShoreA,15Sec,23°C | ISO 868 | 53 |
aging | Test Condition | Test Method | Test Result |
---|---|---|---|
Change rate of tensile strength in air | 100°C,168hr | ASTM D573 | -28 % |
125°C,168hr | ASTM D573 | -61 % | |
100°C,168hr | ISO 188 | -28 % | |
125°C,168hr | ISO 188 | -61 % | |
Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inIRM903Oil | ASTM D471 | -33 |
ShoreA,23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | 4.0 | |
ShoreA,23°C,168hr,inWater | ASTM D471 | 5.0 | |
Shore hardness | ShoreA,23°C,168hr,inEthanol,95% | ISO 1817 | 2.0 |
ShoreA,23°C,168hr,inHydrochloricAcid,10% | ISO 1817 | 4.0 | |
ShoreA,23°C,168hr,inIRM903Oil | ISO 1817 | -33 | |
ShoreA,23°C,168hr,inSodiumHydroxide,50% | ISO 1817 | 4.0 | |
ShoreA,23°C,168hr,inWater | ISO 1817 | 5.0 | |
Change rate of ultimate elongation in air | 100°C,168hr | ASTM D573 | -14 % |
125°C,168hr | ASTM D573 | -70 % | |
Tensile stress change rate | 100°C,168hr,Break | ISO 188 | -14 % |
125°C,168hr,Break | ISO 188 | -70 % | |
Change rate of hardness (Shore) in the air | ShoreA,100°C,168hr | ASTM D573 | -4.0 |
ShoreA,125°C,168hr | ASTM D573 | 8.0 | |
ShoreA,100°C,168hr | ISO 188 | -4.0 | |
ShoreA,125°C,168hr | ISO 188 | 8.0 | |
Change rate of tensile strength in air | 23°C,168hr,inEthanol,95% | ASTM D471 | -17 % |
23°C,168hr,inHydrochloricAcid,10% | ASTM D471 | -1.0 % | |
Change rate of ultimate elongation in air | 23°C,168hr,inIRM903Oil | ASTM D471 | -68 % |
23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | -7.0 % | |
23°C,168hr,在水中 | ASTM D471 | -12 % | |
Tensile stress change rate | 23°C,168hr,inEthanol,95%,Break | ISO 1817 | -3.0 % |
23°C,168hr,inHydrochloricAcid,10%,Break | ISO 1817 | -9.0 % | |
23°C,168hr,inIRM903Oil,Break | ISO 1817 | -68 % | |
23°C,168hr,inSodiumHydroxide,50%,Break | ISO 1817 | -7.0 % | |
23°C,168hr,在水中,Break | ISO 1817 | -12 % | |
Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inEthanol,95% | ASTM D471 | 2.0 |
ShoreA,23°C,168hr,inHydrochloricAcid,10% | ASTM D471 | 4.0 | |
Change rate of tensile strength in air | 23°C,168hr,inIRM903Oil | ASTM D471 | -85 % |
23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | 1.0 % | |
23°C,168hr,在水中 | ASTM D471 | 2.0 % | |
23°C,168hr,inEthanol,95% | ISO 1817 | -17 % | |
23°C,168hr,inHydrochloricAcid,10% | ISO 1817 | -1.0 % | |
23°C,168hr,inIRM903Oil | ISO 1817 | -85 % | |
23°C,168hr,inSodiumHydroxide,50% | ISO 1817 | 1.0 % | |
23°C,168hr,在水中 | ISO 1817 | 2.0 % | |
Change rate of ultimate elongation in air | 23°C,168hr,inEthanol,95% | ASTM D471 | -3.0 % |
23°C,168hr,inHydrochloricAcid,10% | ASTM D471 | -9.0 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.