PEEK KetaSpire® KT-880 FW30 SOLVAY USA
202
- Unit Price:US$ 105,375 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Easy to process｜wear resistant｜Acid resistance｜High purity｜High mobility｜Chemical resistance｜Fatigue resistance｜Filler: Carbon fiber reinforced material｜30%｜Filler by weight
- Application Areas:medical care｜Industrial components｜Electrical applications
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 50 g/10min | |
| limiting pv value | 300000to400000 psi·fpm |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 99 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ISO 527-2 | 180 Mpa | |
| ASTM D638 | 194 Mpa | ||
| elongation | ASTM D638 | 1.8 % | |
| ISO 527-2 | 1.7 % | ||
| Flexural modulus | ASTM D790 | 13500 Mpa | |
| ISO 178 | 13200 Mpa | ||
| bending strength | ASTM D790 | 280 Mpa | |
| ISO 178 | 260 Mpa | ||
| compressive strength | ASTM D695 | 138 Mpa | |
| shear strength | ASTM D732 | 83.0 Mpa | |
| Tensile modulus | ASTM D638 | 13500 Mpa | |
| ISO 527-2 | 16000 Mpa | ||
| coefficient of friction | ASTM D3702 | 0.28 | |
| Wear factor | ASTM D3702 | 46 10^-8mm³/N·m |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ASTM D4812 | 530 J/m |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt viscosity | ASTM D3835 | 150 Pa·s |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Glass Transition Temperature | ISO 11357-2 | 147 °C | |
| melting temperature | ISO 11357-3 | 343 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.