PA66 Zytel® 70G33HS1L BK031 DUPONT JAPAN

Unit Price:US$ 3,190 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
33MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Transaction Guarantee:

Supplier Information

Shenzhen Jufengde Plastic Co., Ltd

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜high strength｜Glass fiber reinforced
Application Areas:Automotive sector
Color:--
Grade:Enhanced level

Material Certification

Technical Data Sheet

Filling analysis	Test Condition	Test Method	Test Result	Test Unit
Top out temperature			210	°C
Emission of Organic Compounds		VDA 277	10.0	µgC/g
Odor		VDA 270	3.00
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	75	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
FMVSS combustion rate		FMVSS 302	B
雾化 - G-value (condensate)		ISO 6452	6.0E-4	g
UL flame retardant rating		UL 94	HB
UL flame retardant rating	UL flame retardant rating		UL 94	HB
Burning rate	1.00 mm	ISO 3795	28	mm/min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	280	Mpa
Bending modulus		ISO 178	9500	Mpa
Tensile strain	Break	ISO 527-2	3.0	%
tensile strength	Break	ISO 527-2	200	Mpa
Tensile modulus		ISO 527-2	11000	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			80	°C
Suggested maximum moisture content			0.20	%
Drying time - hot air dryer			2.0 to 4.0	hr
Processing (melt) temperature			275 to 295	°C
Melt Temperature, Optimum			285	°C
Mold temperature			70 to 120	°C
Mold Temperature, Optimum			100	°C
Maintain pressure			50.0 to 100	Mpa
Maintain pressure	Maintain pressure	Drying Recommended		yes
Hold Pressure Time			3.00	s/mm
Maximum Screw Tangential Speed			12	m/min
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	Across Flow : 55 to 160°C	ISO 11359-2	1.4E-4	cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -40 to 23°C	ISO 11359-2	6.5E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	8.3E-5	cm/cm/°C
			Linear coefficient of thermal expansion	Flow : 55 to 160°C	ISO 11359-2	1.3E-5	cm/cm/°C
				Linear coefficient of thermal expansion	Flow : -40 to 23°C	ISO 11359-2	2.4E-5	cm/cm/°C
				Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow	ISO 11359-2	1.8E-5	cm/cm/°C
Melting temperature		ISO 11357-3	262	°C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	252	°C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	261	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	1.8	%
Water absorption rate	Water absorption rate	Saturation, 23°C, 2.00 mm	ISO 62	5.7	%
Shrinkage rate	Flow	ISO 294-4	0.30	%
Shrinkage rate	Shrinkage rate	横向Flow	ISO 294-4	1.1	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index		UL 746	PLC 1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
ASIAPLAS	US$ 3680 /MT

Supplier Join

Get App

Top

PA66 Zytel® 70G33HS1L BK031 DUPONT JAPAN

Material Description

Material Certification

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index