PC Makrolon® 8025 000000 COVESTRO SHANGHAI
278
- Unit Price:US$ 3,476 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:36MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜High mobility｜Filler: Glass fiber with embossing｜20% filler by weight｜20% filler by weight
- Application Areas:Automotive Applications｜Lighting installation｜electrical equipment
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 136 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 141 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 134 °C | |
| vicat | -- | ISO 306/B50 | 146 °C |
| -- | ISO 306/B120 | 147 °C | |
| ball-indentation hardness | 137°C | IEC 60695-10-2 | Pass |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 4.5E-05 cm/cm/°C |
| TD：23to55°C | ISO 11359-2 | 5.5E-05 cm/cm/°C | |
| thermal conductivity | 23°C | ISO 8302 | 0.23 W/m/K |
| RTI Elec | 1.5mm | UL 746 | 125 °C |
| RTI Imp | 1.5mm | UL 746 | 115 °C |
| RTI Str | 1.5mm | UL 746 | 125 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-2 |
| 6.0mm | UL 94 | V-1 | |
| Burning wire flammability index | 0.75mm | IEC 60695-2-12 | 800 °C |
| 1.5mm | IEC 60695-2-12 | 960 °C | |
| 2.0mm | IEC 60695-2-12 | 960 °C | |
| 3.0mm | IEC 60695-2-12 | 960 °C | |
| 4.0mm | IEC 60695-2-12 | 960 °C | |
| Hot filament ignition temperature | 0.75mm | IEC 60695-2-13 | 850 °C |
| 2.0mm | IEC 60695-2-13 | 875 °C | |
| 3.0mm | IEC 60695-2-13 | 875 °C | |
| Limiting Oxygen Index | ISO 4589-2 | 32 % | |
| ApplicationofFlamefromSmallBurner-Method | 2.00mm | DIN 53438-1,-3 | K1.F1 |
| Burning rate - US-FMVSS | >1.00mm | ISO 3795 | passed |
| FlashIgnitionTemperature | ASTM D1929 | 470 °C | |
| needle flame test | MethodF:1.50mm | IEC 60695-11-5 | 2.0 min |
| MethodF:2.00mm | IEC 60695-11-5 | 2.0 min | |
| MethodF:3.00mm | IEC 60695-11-5 | 2.0 min | |
| MethodK:1.50mm | IEC 60695-11-5 | 1.0 min | |
| MethodK:2.00mm | IEC 60695-11-5 | 1.0 min | |
| MethodK:3.00mm | IEC 60695-11-5 | 2.0 min | |
| SelfIgnitionTemperature | ASTM D1929 | 550 °C |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| electrolytic corrosion | 23°C | IEC 60426 | A1 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C,完全断裂 | ISO 179/1eU | 65 kJ/m² |
| 23°C,完全断裂 | ISO 179/1eU | 55 kJ/m² | |
| Impact strength of cantilever beam gap | 23°C,CompleteBreak | ISO 7391 | 12 kJ/m² |
| Multi axis Instrumented Impact Energy | -30°C | ISO 6603-2 | 10.0 J |
| 23°C | ISO 6603-2 | 20.0 J | |
| Multi axis Instrumented Peak Impact Force | -30°C | ISO 6603-2 | 2800 N |
| 23°C | ISO 6603-2 | 3300 N | |
| Charpy Notched Impact Strength | 23°C,CompleteBreak | ISO 7391 | 12 kJ/m² |
| Impact strength of simply supported beam without notch | -60°C,CompleteBreak | ISO 179/1eU | 65 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | 23°C | IEC 60093 | 1E+16 ohms·cm |
| dielectric strength | 23°C,1.00mm | IEC 60243-1 | 36 KV/mm |
| relative permittivity | 23°C,100Hz | IEC 60250 | 3.30 |
| 23°C,1MHz | IEC 60250 | 3.30 | |
| Dissipation Factor | 23°C,100Hz | IEC 60250 | 1E-03 |
| 23°C,1MHz | IEC 60250 | 9E-03 | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 3 |
| 解决方案B | IEC 60112 | PLC 4 | |
| Surface Resistivity | IEC 60093 | 1E+16 ohms |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | 23°C | ISO 1183 | 1.34 g/cm³ |
| Apparent density | ISO 60 | 0.69 g/cm³ | |
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 6.5 g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 6.00 cm3/10min |
| shrinkage rate | TD | ISO 2577 | 0.30-0.45 % |
| MD | ISO 2577 | 0.30-0.45 % | |
| TD:2.00mm3 | ISO 294-4 | 0.35 % | |
| MD:2.00mm3 | ISO 294-4 | 0.55 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.24 % |
| 平衡,23°C,50%RH | ISO 62 | 0.10 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strain | 屈服,23°C | ISO 527-2/50 | 3.5 % |
| 断裂,23°C | ISO 527-2/5 | 6.5 % | |
| Tensile creep modulus | 1hr | ISO 899-1 | 3700 Mpa |
| 1000hr | ISO 899-1 | 3500 Mpa | |
| flexural modulus | 23°C | ISO 178 | 3700 Mpa |
| bending strength | 3.5%Strain,23°C | ISO 178 | 95.0 Mpa |
| 23°C | ISO 178 | 100 Mpa | |
| Bending Strain | 23°C | ISO 178 | 5.4 % |
| Tensile modulus | 23°C | ISO 527-2/1 | 4000 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2/50 | 58.0 Mpa |
| 断裂,23°C | ISO 527-2/5 | 50.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.