PA66 Leona™ FG173 NC ASAHI JAPAN
217
- Unit Price:US$ 4,366 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:100MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜Glass fiber reinforced｜Filler: Glass fiber reinforced material｜Glass fiber content is 30% GF｜Flame retardant grade UL94 V-0
- Application Areas:Hose｜Joint｜switch｜Electronic field｜Electrical field｜Electrical components｜Electrical/Electronic Applications｜switch｜Laptop case｜Joint｜switch｜Other electrical and electronic materials
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 100 |
| M级 | ASTM D785 | 100 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.82MPa,干 | ASTM D-648 | 252 °C |
| 0.46MPa,干 | ASTM D-648 | 260 °C | |
| UL flame retardant rating | 干 | UL 94 | V-0 |
| Linear coefficient of thermal expansion | 干 | ASTM D-696 | 3 |
| Heat Deflection Temperature | 0.45MPa,未退火 | ASTM D648 | 260 °C |
| 0.45MPa,未退火 | ISO 75-2/B | 262 °C | |
| 1.8MPa,未退火 | ASTM D648 | 252 °C | |
| 1.8MPa,未退火 | ISO 75-2/A | 245 °C | |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 3E-05 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 960 °C |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | 湿 | 0.6 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 50 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Wear factor | 湿 | ASTM D-1044 | 29 |
| shrinkage rate | 干 | 旭化成方法 | 0.3-0.7 % |
| TD | 内部方法 | 0.70 % | |
| MD | 内部方法 | 0.30 % | |
| 吸水率(饱和,23°C) | 内部方法 | -- % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | -- % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric strength | ASTM D149 | 28 KV/mm | |
| IEC 60243-1 | 28 KV/mm | ||
| Compared to the Leakage Tracking Index (CTI) | 3.00mm | IEC 60112 | PLC 2 |
| Surface Resistivity | ASTM D257 | 1E+14 ohms | |
| IEC 60093 | 1E+14 ohms | ||
| volume resistivity | ASTM D257 | 1E+15 ohms·cm | |
| 23°C | IEC 60093 | 1E+15 ohms·cm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | 干(湿) | ASTM D-790 | 250(221) Mpa |
| Elongation at break | 干(湿) | ASTM D-638 | 2.5(2.7) % |
| Impact strength of cantilever beam gap | 干(湿) | ASTM D-256 | 88(98) J/m |
| flexural coefficient | 干(湿) | ASTM D-790 | 10.8(8.3) GPa |
| tensile strength | 干(湿) | ASTM D-638 | 167(142) Mpa |
| Rockwell hardness | 干(湿) | ASTM D-785 | 100(60) M Scale |
| Tensile strain | 断裂,23°C | ISO 527-2 | 2.0 % |
| flexural modulus | ASTM D790 | 10800 Mpa | |
| 23°C | ISO 178 | 10300 Mpa | |
| bending strength | ASTM D790 | 250 Mpa | |
| 23°C | ISO 178 | 259 Mpa | |
| Taber abraser | 1000Cycles | ASTM D1044 | -- mg |
| Tensile modulus | 23°C | ISO 527-2 | 11700 Mpa |
| tensile strength | ASTM D638 | 167 Mpa | |
| 断裂,23°C | ISO 527-2 | 174 Mpa | |
| elongation | 断裂 | ASTM D638 | 2.5 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.