Material Description
- Material Properties:UV resistance｜Weather resistance｜Medium viscosity｜VOC
- Application Areas:Industrial machinery｜Automotive sector｜Engineering accessories｜Engine parts｜Shell｜Application in the automotive field
- Color:--
- Grade:Injection grade
Technical Data Sheet
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M-Scale | ASTM D785 | 80 |
| R-Scale | ASTM D785 | 115 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD | ASTMD696 | 1E-04 cm/cm/°C |
| Hot deformation temperature | 0.45MPa,Unannealed | ASTM D648 | 158 °C |
| 0.45MPa,Unannealed | ISO 75-2/B | 154 °C | |
| 1.8MPa,Unannealed | ASTM D648 | 110 °C | |
| 1.8MPa,Unannealed | ISO 75-2/A | 97.0 °C |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 9.0 g/10min |
| Shrinkage rate | MD | Internal Method | 1.6-2.0 % |
| Water absorption rate | 23°C,24hr,50%RH | ASTM D570 | 0.20 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface resistivity | ASTM D257 | 1.0E+16-1.0E+17 ohms | |
| Volume resistivity | 23°C | ASTM D257 | 1.0E+15-1.0E+16 ohms·cm |
| Dielectric strength | ASTM D149 | 19 KV/mm | |
| Arc resistance | ASTM D495 | 250 sec |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2550 Mpa | |
| tensile strength | Yield | ISO 527-2 | 63.0 Mpa |
| -- | ASTM D638 | 62.0 Mpa | |
| elongation | Break | ASTMD638 | 35 % |
| Bending modulus | -- | ASTM D790 | 2500 Mpa |
| -- | ISO 178 | 2450 Mpa | |
| bending strength | ASTM D790 | 88.0 Mpa | |
| Taber abraser | ASTM D1044 | 14.0 mg |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.