Material Description

Material Properties:heat-resisting｜transparent｜High impact resistance
Application Areas:Lighting fixtures｜Food containers｜Bottle cap
Color:--
Grade:Transparent level

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
transmissivity		ASTM D1003	87.0to91.0 %

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA2	90.0 kJ/m²
	Charpy Notched Impact Strength	-30°C	ISO 179/1eA2	13.0 kJ/m²
		Charpy Notched Impact Strength	23°C	ISO 179/1eU2	NoBreak
		Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eU2	NoBreak
Impact strength of cantilever beam gap	23°C	ISO 180/4A	88 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180	NoBreak

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.6mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	3.2mm	UL 94	HB
BurningBehav.at1.6mmnom.thickn	1.60mm,UL	ISO 12102	HB
Burning Behav.atthicknessh	3.20mm,UL	ISO 12102	HB
Limiting Oxygen Index (LOI)		ISO 4589-22	26 %

mechanical properties	Test Condition	Test Method	Test Result
Nominal fracture strain		ISO 527-22	>50 %
Bending modulus		ISO 178	2400 Mpa
bending strength		ISO 178	97.0 Mpa
Tensile modulus		ISO 527-2/50	2300 Mpa
Tensile modulus	Tensile modulus		ISO 527-22	2300 Mpa
tensile strength	Yield	ISO 527-2/50	60.0 Mpa
	tensile strength	Yield	ISO 527-22	60.0 Mpa
	tensile strength	tensile strength	Break	ISO 527-2/50	71.0 Mpa
Tensile strain	Yield	ISO 527-2/50	6.0 %
	Tensile strain	Yield	ISO 527-22	6.0 %
	Tensile strain	Tensile strain	Break	ISO 527-2/50	150 %

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Annealed	ISO 75-2/B	144 °C
	Hot deformation temperature	0.45MPa	ISO 75-22	145 °C
		Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	125 °C
			Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	141 °C
			Hot deformation temperature	Hot deformation temperature	1.8MPa	ISO 75-22	131 °C
Vicat softening temperature		ISO 306/B50	149 °C
Vicat softening temperature	Vicat softening temperature	50N	ISO 3062	149 °C
Ball pressure temperature		IEC 60335-1	125 °C
Linear coefficient of thermal expansion	MD	ISO 11359-22	7E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183/A	1.20 g/cm³
density	density		ISO 11832	1200 kg/m3
melt mass-flow rate	300°C/1.2kg	ISO 1133	10 g/10min
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 11332	8.00 cm3/10min
Shrinkage rate	MD	ISO 294-4	0.50-0.70 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		IEC 600932	>1.0E+13 ohms·m
Dielectric strength		IEC 60243-12	17 KV/mm
Relative permittivity	100Hz	IEC 602502	3.00
Relative permittivity	Relative permittivity	1MHz	IEC 602502	3.00
Dissipation factor	100Hz	IEC 602502	1E-03
Dissipation factor	Dissipation factor	1MHz	IEC 602502	2E-03
Compared to the anti leakage trace index	2.00mm	IEC 60112	PLC 2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC CALIBRE™ 201-10 STYRON US

Material Description

Technical Data Sheet Compare

Technical Data Sheet