Material Properties:Low temperature resistance｜High mobility
Application Areas:Automotive components｜Electronic and electrical accessories｜Good molding function
Color:--
Grade:--

Technical Data Sheet Compare

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45MPa 未退火	ISO 75-2/B	258 °C
	Heat Deflection Temperature	1.8MPa 未退火	ASTM D648	241 °C
	Heat Deflection Temperature	Heat Deflection Temperature	1.8MPa 未退火	ISO 75-2/A	253 °C

Basic performance	Test Condition	Test Method	Test Result
shrinkage rate	，Across Flow: 24 hr	ISO 294-4	0.22 %
Water absorption rate		ASTM D570	0.0100 %
density		ASTM D792A	1.58 g/cm
shrinkage rate	，Flow: 24 hr	ASTM D955	0.10 %
	shrinkage rate	，Flow: 24 hr	ISO 294-4	0.18 %
	shrinkage rate	shrinkage rate	，Across Flow: 24 hr	ISO 294-4	0.20 %

Physical properties	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	3.18 mm	ASTM D256	384 J/m

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	17500 Mpa
Tensile modulus	Tensile modulus		ISO 527-2	18400 Mpa
tensile strength		ASTM D638	254 Mpa
tensile strength	tensile strength		ISO 527-2	256 Mpa
Elongation at break		ASTM D638	1.9 %
bending strength	，-	ASTM D790	372 Mpa
bending strength	bending strength	，-	ISO 178	371 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.