Material Properties:High rigidity｜High impact resistance｜High mobility｜Impact resistance｜filler｜Mineral filler｜12%｜Filler by weight
Application Areas:Car bumper｜Automotive sector｜Automotive External Parts｜Car exterior decoration｜Food packaging｜film
Color:--
Grade:--

Technical Data Sheet Compare

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45 MPa,未退火	ISO 75-2/B	80 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.8 MPa,未退火	ISO 75-2/A	47 °C
vicat		ISO 306/A	122 °C
vicat	vicat		ISO 306/B	40 °C
Linear coefficient of thermal expansion	MD：-30 到 80℃	内部方法	6.8E-05 cm/cm/℃

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	230℃/2.16 kg	ISO 1183	40 g/10 min
shrinkage rate		内部方法	0.80 %
ball-indentation hardness		ISO 2039-1	28.0 Mpa

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	-20℃,注塑	ISO 179/1eA	5.5 kJ/m²
tensile strength	tensile strength	23℃,注塑	ISO 179/1eA	31 kJ/m²
Impact strength of simply supported beam without notch	-20℃,注塑	ISO 179/1eU	30 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23℃,注塑	ISO 179/1eU	无断裂 kJ/m²
Impact strength of cantilever beam gap	-20℃,注塑	ISO 180/1A	5.5 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23℃,注塑	ISO 180/1A	33 kJ/m²
Tensile modulus	注塑	ISO 527-2/1	1150 Mpa
tensile strength	屈服,注塑	ISO 527-2/50	16.0 Mpa
	tensile strength	拉伸应变，屈服,注塑	ISO 527-2/50	5.2 %
		tensile strength	弯曲模量，注塑	ISO 178	1150 Mpa
			tensile strength	弯曲应力，注塑	ISO 868	21 Mpa
			tensile strength	tensile strength	简支梁缺口冲击强度，-30℃,注塑	ISO 179/1eA	4 kJ/m²

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.