PPO FLEX NORYL™ SE1X-701 SABIC INNOVATIVE SHANGHAI

411

Unit Price:US$ 4,274 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
76MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details
Material Comparison:
PPO PF1X KAOSO U.S.

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜High temperature resistance
Application Areas:Electronic and electrical components
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C, Energy at Peak	ASTM D3763	51.0 J
Dart impact	Dart impact	-30°C, Energy at Peak	ASTM D3763	32.0 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5 mm	UL 94	V-1
UL flame retardant rating	UL flame retardant rating	6.0 mm	UL 94	V-0
Radiation board grade			RP100

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Yield, 100 mm Span	ASTM D790	102 Mpa
Bending modulus	100 mm Span	ASTM D790	2500 Mpa
elongation	Break	ASTM D638	20 %
elongation	elongation	Yield	ASTM D638	8.1 %
tensile strength	Break	ASTM D638	53.0 Mpa
tensile strength	tensile strength	Yield	ASTM D638	67.0 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			105 to 110 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			30 to 70 %
Temperature at the rear of the barrel			250 to 300 °C
Temperature in the middle of the barrel			260 to 305 °C
Temperature at the front of the material cylinder			270 to 310 °C
Spray nozzle temperature			280 to 310 °C
Processing (melt) temperature			280 to 310 °C
Mold temperature			75 to 105 °C
Back pressure			0.300 to 0.700 Mpa
Screw speed			20 to 100 rpm

thermal performance	Test Condition	Test Method	Test Result
RTI		UL 746	110 °C
RTI Imp		UL 746	105 °C
RTI Elec		UL 746	110 °C
Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	117 °C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	126 °C

Physical properties	Test Condition	Test Method	Test Result
Outdoor applicability		UL 746C	f1
Water absorption rate	24 hr	ASTM D570	0.060 %
Shrinkage rate	Across FlowFlow 2	Internal Method	0.50 - 0.70 %
Shrinkage rate	Shrinkage rate	Flow : 3.20 mm	Internal Method	0.50 - 0.70 %

Electrical performance	Test Condition	Test Method	Test Result
Dissipation factor	60 Hz	ASTM D150	3.4E-3
Dissipation factor	Dissipation factor	50 Hz	ASTM D150	3.4E-3
Dielectric constant	1 MHz	ASTM D150	2.46
Dielectric constant	Dielectric constant	50 kHz	ASTM D150	2.52
Surface resistivity		ASTM D257	> 1.0E+15 ohms
Dissipation factor	1 MHz	ASTM D150	2.1E-3
Arc resistance		ASTM D495	PLC 6
Compared to the anti leakage trace index		UL 746	PLC 1
High voltage arc tracing rate		UL 746	PLC 4
Dielectric constant	60 Hz	ASTM D150	2.52
Dielectric strength	3.20 mm, in Oil	ASTM D149	18 KV/mm
Volume resistivity		ASTM D257	2.3E+16 ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PPO FLEX NORYL™ SE1X-701 SABIC INNOVATIVE SHANGHAI

Material Description

Technical Data Sheet Compare

Technical Data Sheet