PBT NOVADURAN™  5010N5 MITSUBISHI ENGINEERING JAPAN

221
  • Unit Price:US$ 2,585 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    10MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:--
  • Application Areas:--
  • Color:--
  • Grade:Flame retardant grade

Material Certification

UL

Technical Data Sheet

machinabilityTest ConditionTest MethodTest Result
Mold temperature60-80 °C
Screw speed80-150 rpm
Processing temperature245 °C
Processing temperature240 °C
Processing temperature250 °C
Processing temperature235 °C
Dry conditions热风干燥 120℃---5-8小时 140℃---约4小时
mechanical propertiesTest ConditionTest MethodTest Result
Elongation at BreakASTM D638/ISO 52730 %
bending strengthASTM D790/ISO 17890 kg/cm²(MPa)[Lb/in²]
Bending modulusASTM D790/ISO 1782600 kg/cm²(MPa)[Lb/in²]
Tensile modulusASTM D638/ISO 5272400 kg/cm²(MPa)[Lb/in²]
thermal performanceTest ConditionTest MethodTest Result
Linear coefficient of thermal expansionASTM D696/ISO 113591.E-04 mm/mm.℃
Combustibility (rate)UL 94V-2
Physical propertiesTest ConditionTest MethodTest Result
Water absorption rateASTM D570/ISO 620.08 %
Shrinkage rateASTM D9551.4 %
densityASTM D792/ISO 11831.42
Electrical performanceTest ConditionTest MethodTest Result
Volume resistivityASTM D257/IEC 600931.E+14 Ω.cm
Dielectric constantASTM D150/IEC 602503.2
Surface resistivityASTM D257/IEC 600931.E+15 Ω
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.