PC TARFLON™ GZ2540 IDEMITSU JAPAN
216
- Unit Price:US$ 2,691 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:40.5MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant
- Application Areas:Automotive Applications｜Home appliance components
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | 内部方法 | 0.6 % | |
| 内部方法 | 0.12 % | ||
| Water absorption rate | ISO 62 | 0.1 % | |
| Shrinkage rate | 内部方法 | 0.60 % | |
| 内部方法 | 0.12 % | ||
| Water absorption rate | ISO 62 | 0.10 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 75 |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | GF增强／非溴／非磷／阻燃 V-0 | ||
| purpose | 打印机和复印机零部件、液晶投影仪零部件、手机外壳、电动工具、游戏机外壳 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-1 | |
| UL 94 | V-0 | ||
| UL 94 | V-0 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO Shortcut | >PC-GF40< |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 75 | |
| tensile strength | ISO 527-2 | 130 Mpa | |
| Tensile strain | ISO 527-2 | 2 % | |
| Flexural modulus | ISO 178 | 11300 Mpa | |
| bending strength | ISO 178 | 185 Mpa | |
| Charpy Notched Impact Strength | ISO 179 | 11 kJ/m² | |
| tensile strength | ISO 527-2 | 130 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 2.0 % | |
| Flexural modulus | ISO 178 | 11300 Mpa | |
| bending strength | ISO 178 | 185 Mpa | |
| elongation at break | ASTM D638/ISO 527 | 2 % | |
| tensile strength | ASTM D638/ISO 527 | 130 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | M75 | |
| Flexural modulus | ASTM D790/ISO 178 | 11.3 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 185 kg/cm²(MPa)[Lb/in²] |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric constant | IEC 60250 | 2.95 | |
| arc resistance | ASTM D495 | 110 sec | |
| dielectric strength | IEC 60243-1 | > 22 KV/mm | |
| Volume resistivity | ASTM D257 | >1.0E+16 ohms·cm | |
| dielectric strength | IEC 60243-1 | >22 KV/mm | |
| dielectric constant | IEC 60250 | 3.45 | |
| Dissipation Factor | IEC 60250 | 9E-03 | |
| dielectric constant | ASTM D150/IEC 60250 | 2.95 | |
| arc resistance | ASTM D495/IEC 60112 | 110 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.51 | |
| Shrinkage rate | ASTM D955 | 0.12-0.6 % | |
| Water absorption rate | ASTM D570/ISO 62 | 0.1 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/A | 147 °C | |
| Linear coefficient of thermal expansion | ASTM D696 | 0.000019 cm/cm/℃ | |
| UL flame retardant rating | UL 94 | V-0 | |
| Heat distortion temperature | ISO 75-2/A | 147 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 1.9E-05 cm/cm/°C | |
| Combustibility (rate) | UL 94 | V-0/1.5（black） | |
| Heat distortion temperature | ASTM D648/ISO 75 | 147 ℃（℉） | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 1.9 mm/mm.℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.