PPA AMODEL® A-6135 HN BK324 SOLVAY USA

283

Unit Price:US$ 5,657 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
43MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Chemical resistance｜Low moisture absorption
Application Areas:Shell｜Vehicle electronics
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	60 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180	62 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
bending strength	3.5%Strain,150°C	ISO 178	123 Mpa
bending strength	bending strength	3.5%Strain,175°C	ISO 178	112 Mpa
compressive strength		ASTM D695	148 Mpa
shear strength		ASTM D732	87.6 Mpa
Poisson's ratio			7.58 0.39
Tensile strain	Break,150°C	ISO 527-2	4.9 %
Tensile strain	Tensile strain	Break,175°C	ISO 527-2	4.7 %
Bending modulus		ASTM D790	11400 Mpa
	Bending modulus	23°C	ISO 178	11400 Mpa
		Bending modulus	100°C	ISO 178	6600 Mpa
			Bending modulus	150°C	ISO 178	4900 Mpa
			Bending modulus	Bending modulus	175°C	ISO 178	4600 Mpa
bending strength		ASTM D790	310 Mpa
	bending strength	3.5%Strain,23°C	ISO 178	300 Mpa
	bending strength	bending strength	3.5%Strain,100°C	ISO 178	170 Mpa
Tensile modulus		ASTM D638	13800 Mpa
	Tensile modulus	23°C	ISO 527-2	11500 Mpa
		Tensile modulus	100°C	ISO 527-2	7310 Mpa
			Tensile modulus	150°C	ISO 527-2	6270 Mpa
			Tensile modulus	Tensile modulus	175°C	ISO 527-2	5310 Mpa
tensile strength		ASTM D638	203 Mpa
	tensile strength	Break,23°C	ISO 527-2	211 Mpa
		tensile strength	Break,24°C	ISO 527-2	121 Mpa
			tensile strength	Break,150°C	ISO 527-2	92.4 Mpa
			tensile strength	tensile strength	Break,175°C	ISO 527-2	82.0 Mpa
elongation	Break	ASTM D638	1.9 %
Tensile strain	Break,23°C	ISO 527-2	2.0 %
Tensile strain	Tensile strain	Break,24°C	ISO 527-2	4.3 %

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD：100to200°C	ASTME831	1E-04 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	303 °C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	288 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed,3.20mm	ASTM D648	291 °C
Melting temperature		ISO 11357-3	310 °C
Melting temperature	Melting temperature		ASTM D570	310 °C
Linear coefficient of thermal expansion	MD：0to100°C	ASTME831	2.2E-05 cm/cm/°C
	Linear coefficient of thermal expansion	MD：100to200°C	ASTME831	1.6E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：0to100°C	ASTME831	6.1E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD	ASTM D955	0.60 %
	Shrinkage rate	TD	ASTM D955	0.90 %
		Shrinkage rate	TD	ISO 294-4	1.0 %
		Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.50 %
Water absorption rate	24hr	ASTM D570	0.30 %
Water absorption rate	Water absorption rate	23°C,24hr	ISO 62	0.29 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	125

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PPA AMODEL® A-6135 HN BK324 SOLVAY USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet