PC Makrolon® RX1805 COVESTRO SHANGHAI
232
- Unit Price:US$ 7,366 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:30MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:transparent
- Application Areas:Medical supplies
- Color:--
- Grade:--
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 114 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | IEC 60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 6.5E-05 cm/cm/°C | |
| vicat | ISO 306/B120 | 145 °C | |
| thermal conductivity | ISO 8302 | 0.20 W/m/K | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 6.5E-05 cm/cm/°C | |
| vicat | ISO 306/B50 | 144 °C | |
| Glass Transition Temperature | ISO 11357-2 | 145 °C | |
| Heat Deflection Temperature | ISO 75-2/A | 126 °C | |
| ISO 75-2/B | 138 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| FlashIgnitionTemperature | ASTM D1929 | 480 °C | |
| SelfIgnitionTemperature | ASTM D1929 | 550 °C | |
| Limiting Oxygen Index | ISO 4589-2 | 27 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 7391 | 70 kJ/m² | |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 70.0 J | |
| Multi axis Instrumented Peak Impact Force | ISO 6603-2 | 6600 N | |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 65.0 J | |
| Multi axis Instrumented Peak Impact Force | ISO 6603-2 | 5700 N | |
| Impact strength of simply supported beam without notch | ISO 179/1eU | NoBreak | |
| Impact strength of cantilever beam gap | ISO 7391 | 15 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179/1eU | NoBreak | |
| ISO 179/1eU | NoBreak | ||
| Charpy Notched Impact Strength | ISO 7391 | 16 kJ/m² | |
| ISO 7391 | 80 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | ISO 178 | 98.0 Mpa | |
| Bending Strain | ISO 178 | 7.1 % | |
| bending strength | ISO 178 | 73.0 Mpa | |
| Nominal tensile fracture strain | ISO 527-2/50 | >50 % | |
| flexural modulus | ISO 178 | 2400 Mpa | |
| Tensile strain | ISO 527-2/50 | 130 % | |
| tensile strength | ISO 527-2/50 | 75.0 Mpa | |
| Tensile strain | ISO 527-2/50 | 6.3 % | |
| Tensile modulus | ISO 527-2/1 | 2400 Mpa | |
| tensile strength | ISO 527-2/50 | 67.0 Mpa |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | ISO 62 | 0.30 % | |
| shrinkage rate | ISO 294-4 | 0.70 % | |
| ISO 294-4 | 0.70 % | ||
| ISO 2577 | 0.60-0.80 % | ||
| ISO 2577 | 0.60-0.80 % | ||
| melt mass-flow rate | ISO 1133 | 6.5 g/10min | |
| Melt volume flow rate | ISO 1133 | 6.00 cm3/10min | |
| density | ISO 1183 | 1.20 g/cm³ | |
| Apparent density | ISO 60 | 0.66 g/cm³ | |
| Water absorption rate | ISO 62 | 0.12 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.