PEI ULTEM™ 3452-1000 SABIC INNOVATIVE US

257

Unit Price:US$ 21,629 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
15MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Dimensional stability｜Middle flow
Application Areas:Electrical components｜Sports equipment
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Reverse notch impact	3.20 mm	ASTM D256	220 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	3.0 mm	UL 94	5VA
UL flame retardant rating	UL flame retardant rating	0.77 mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Break, 100 mm Span	ASTM D790	179 Mpa
Bending modulus	100 mm Span	ASTM D790	12400 Mpa
elongation	Break	ASTM D638	1.4 %
tensile strength	Break	ASTM D638	131 Mpa

injection	Test Condition	Test Method	Test Result
Temperature in the middle of the barrel			340 to 400 °C
Temperature at the rear of the barrel			330 to 400 °C
Suggested injection volume			40 to 60 %
Suggested maximum moisture content			0.020 %
drying time			4.0 to 6.0 hr
drying temperature			150 °C
Temperature at the front of the material cylinder			345 to 400 °C
Spray nozzle temperature			345 to 400 °C
Processing (melt) temperature			350 to 400 °C
Mold temperature			135 to 165 °C
Back pressure			0.300 to 0.700 Mpa
Screw speed			40 to 70 rpm
Exhaust hole depth			0.025 to 0.076 mm

thermal performance	Test Condition	Test Method	Test Result
RTI		UL 746	180 °C
RTI Imp		UL 746	180 °C
RTI Elec		UL 746	180 °C
Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	212 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.30 - 0.50 %
Shrinkage rate	Shrinkage rate	Flow : 3.20 mm	Internal Method	0.15 - 0.25 %
melt mass-flow rate	337°C/6.6 kg	ASTM D1238	4.6 g/10 min

Electrical performance	Test Method	Test Result
Hot wire ignition	UL 746	PLC 1
High voltage arc tracing rate	UL 746	PLC 4
High arc combustion index	UL 746	PLC 4
Compared to the anti leakage trace index	UL 746	PLC 4
Arc resistance	ASTM D495	PLC 5

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.