Material Description

Material Properties:Flame retardant｜High impact resistance｜High temperature resistance
Application Areas:Electrical field｜Electronic field
Color:--
Grade:Flame retardant grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C	ISO 180/1A	21	kJ/m²
	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	11	kJ/m²
		Impact strength of cantilever beam gap	23°C,6.40mm	ASTM D256	200	J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	230	J/m
Charpy Notched Impact Strength	23°C	ISO 179	22	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179	12	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	2.5mm	UL 94	5VA
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Yield4	ASTM D638	38.6	Mpa
bending strength	--6	ISO 178	58.0	Mpa
bending strength	bending strength	--5	ASTM D790	60.7	Mpa
Bending modulus	--6	ISO 178	2000	Mpa
Bending modulus	Bending modulus	--5	ASTM D790	2410	Mpa
elongation	Break	ISO 527-2/50	15	%
elongation	elongation	Break4	ASTM D638	30	%
tensile strength	Break	ISO 527-2/50	29.0	Mpa
tensile strength	tensile strength	Yield	ISO 527-2/50	38.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	MD	ISO 11359-2	8.5E-05	cm/cm/°C
Vicat softening temperature	--	ISO 306/B50	96.0	°C
	Vicat softening temperature	--	ISO 306/A50	103	°C
	Vicat softening temperature	Vicat softening temperature	--	ASTM D15257	104	°C
Hot deformation temperature	1.8MPa,Annealed	ASTMD648	96.0	°C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	86.0	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	85.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate		ISO 294-4	0.30-0.60	%
Melt Volume Flow Rate (MVR)	220°C/10.0kg	ISO 1133	27.0	cm3/10min
melt mass-flow rate	200°C/5.0kg	ASTM D1238	2.8	g/10min
density	23°C	ISO 1183	1.19	g/cm³
density	density	--3	ASTM D792	1.19	g/cm³
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	98

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.