PC LNP™ LUBRILOY™ D20001-BK8833 SABIC INNOVATIVE US

213

Unit Price:US$ 4,437 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
36.6MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:wear resistant
Application Areas:Electrical appliances｜Plastic bag｜Aerospace Applications
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C4	ISO 180/1U	100 kJ/m²
Dart impact	23°C, Energy at Peak	ASTM D3763	51.0 J
Suspended wall beam without notch impact strength	23°C	ASTM D4812	1600 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5 mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
Wear factor		ASTM D3702	6.0E+6 10^-8 mm³/N·m
Friction coefficient	Static	ASTM D3702	0.22
Friction coefficient	Friction coefficient	Dynamic	ASTM D3702	0.090
bending strength	--	ISO 178	102 Mpa
bending strength	bending strength	--	ASTM D790	103 Mpa
Bending modulus	--	ISO 178	2800 Mpa
Bending modulus	Bending modulus	--	ASTM D790	2820 Mpa
elongation	Break	ISO 527-2	6.7 %
	elongation	Break	ASTM D638	6.5 %
		elongation	Yield	ISO 527-2	4.3 %
		elongation	elongation	Yield	ASTM D638	4.5 %
tensile strength	Break	ISO 527-2	54.0 Mpa
	tensile strength	Break	ASTM D638	60.0 Mpa
		tensile strength	Yield	ISO 527-2	62.0 Mpa
		tensile strength	tensile strength	Yield	ASTM D638	67.0 Mpa
Tensile modulus	--	ISO 527-2/1	2600 Mpa
Tensile modulus	Tensile modulus	--2	ASTM D638	2550 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			80 °C
drying time			4.0 to 6.0 hr
Suggested maximum moisture content			0.020 %
Temperature at the rear of the barrel			250 to 260 °C
Temperature in the middle of the barrel			255 to 265 °C
Temperature at the front of the material cylinder			260 to 270 °C
Processing (melt) temperature			255 to 290 °C
Mold temperature			40 to 65 °C
Back pressure			0.200 to 0.300 Mpa
Screw speed			30 to 60 rpm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	97.0 °C
	Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	89.0 °C
	Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span4	ISO 75-2/Af	94.0 °C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	6.6E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	6.7E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	6.7E-5 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.12 %
Shrinkage rate	Flow : 24hr	ISO 294-4	0.53 %
	Shrinkage rate	横向Flow : 24hr	ISO 294-4	0.57 %
		Shrinkage rate	Across FlowFlow : 24hr	ASTM D955	0.60 %
		Shrinkage rate	Shrinkage rate	Flow : 24hr	ASTM D955	0.50 %
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ASTM D1238	15.7 cm3/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.