PC/PBT VALOX™ 3706-WH6E293 SABIC INNOVATIVE SHANGHAI
212
- Unit Price:US$ 3,443 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:109MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Impact modification
- Application Areas:Lawn equipment｜Garden equipment｜Plastic bag｜Electrical field｜Electronic field｜Electrical appliances｜Architectural application field｜Outdoor applications｜Lighting applications｜Outdoor applications
- Color:--
- Grade:--
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTM D648 | 127 °C |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 85.0 °C | |
| vicat | ASTM D15255 | 135 °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 7.9E-05 cm/cm/°C |
| TD：-40到40°C | ASTME831 | 8.6E-05 cm/cm/°C | |
| RTI Elec | UL 746 | 100 °C | |
| RTI Imp | UL 746 | 85.0 °C | |
| RTI Str | UL 746 | 100 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| 2.5mm | UL 94 | 5VA |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 670 J/m |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 49.7 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 4 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 2 |
| arc resistance | ASTM D495 | PLC6 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.30 g/cm³ | |
| melt mass-flow rate | 266°C/5.0kg | ASTM D1238 | 19 g/10min |
| Melt volume flow rate | 265°C/5.0kg | ISO 1133 | 17.0 cm3/10min |
| shrinkage rate | MD：3.20mm | 内部方法 | 1.2-1.4 % |
| TD：3.20mm | 内部方法 | 1.2-1.4 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 1970 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 49.0 Mpa |
| 断裂 | ASTM D638 | 39.3 Mpa | |
| elongation | 屈服 | ASTM D638 | 6.0 % |
| 断裂 | ASTM D638 | 50 % | |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 2000 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 78.6 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.