Material Description
- Material Properties:Hydrolysis resistance｜High temperature resistance｜Aging resistance
- Application Areas:Bottle cap｜Automotive Applications｜Electrical applications
- Color:--
- Grade:--
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 190 °C |
| RTI Elec | UL 746 | 115 °C | |
| RTI Imp | UL 746 | 115 °C | |
| RTI | UL 746 | 115 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.75 mm | UL 94 | V-2 |
| 1.5 mm | UL 94 | V-0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 2100 J/m |
| Reverse notch impact | 3.20 mm | ASTM D256 | 2100 J/m |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 337°C/6.6 kg | ASTM D1238 | 24 g/10 min |
| shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.50 - 0.70 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 4 | |
| High arc combustion index (HAI) | UL 746 | PLC 4 | |
| Hot wire ignition (HWI) | UL 746 | PLC 0 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 135 °C | ||
| drying time | 4.0 to 6.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 40 to 60 % | ||
| Temperature at the rear of the barrel | 340 to 360 °C | ||
| Temperature in the middle of the barrel | 345 to 365 °C | ||
| Temperature at the front of the material cylinder | 350 to 370 °C | ||
| Spray nozzle temperature | 350 to 370 °C | ||
| Processing (melt) temperature | 350 to 370 °C | ||
| mold temperature | 135 to 165 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| screw speed | 40 to 70 rpm | ||
| Exhaust hole depth | 0.025 to 0.076 mm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 屈服 | ASTM D638 | 96.0 Mpa |
| elongation | 断裂 | ASTM D638 | 70 % |
| flexural modulus | 100 mm 跨距 | ASTM D790 | 3170 Mpa |
| bending strength | 屈服, 100 mm 跨距 | ASTM D790 | 144 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.