PA66 Amilan® CM3001G33 B3 TORAY SHENZHEN
242
- Unit Price:US$ 2,611 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:21MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Medium viscosity
- Application Areas:Electrical field｜Electronic field｜Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M -Sale, 23°C | ISO 2039-2 | 97 |
| R -Sale, 80°C | ISO 2039-2 | 24 | |
| R -Sale, 23°C | ISO 2039-2 | 121 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 262 °C |
| Melting temperature | DSC | 265 °C | |
| Linear coefficient of thermal expansion | Flow | ISO 11359-2 | 2.0E-5 - 3.0E-5 cm/cm/°C |
| specific heat | 1800 J/kg/°C | ||
| thermal conductivity | 0.40 W/m/K |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.79 mm | UL 94 | HB |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | 23°C | ISO 1183 | 1.37 g/cm³ |
| Shrinkage rate | 横向Flow : 3.00 mm | Internal Method | 0.60 - 0.90 % |
| Flow : 3.00 mm | Internal Method | 0.20 - 0.50 % | |
| Water absorption rate | 24 hr, 23°C | ISO 62 | 0.60 % |
| Saturation, 23°C | ISO 62 | 5.5 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1.0E+13 ohms·cm | |
| Dielectric strength | IEC 60243-1 | 20 KV/mm | |
| Dielectric constant | 23°C, 50 Hz | IEC 60250 | 4.60 |
| 23°C, 1 kHz | IEC 60250 | 4.40 | |
| 23°C, 1 MHz | IEC 60250 | 3.90 | |
| Dissipation factor | 23°C, 50 Hz | IEC 60250 | 0.020 |
| 23°C, 1 kHz | IEC 60250 | 0.020 | |
| 23°C, 1 MHz | IEC 60250 | 0.020 | |
| Arc resistance | UL 746 | 114 sec |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | -40°C | ISO 527-2 | 235 Mpa |
| 23°C | ISO 527-2 | 190 Mpa | |
| 80°C | ISO 527-2 | 120 Mpa | |
| Tensile strain | Break, -40°C | ISO 527-2 | 2.0 % |
| Break, 23°C | ISO 527-2 | 2.5 % | |
| Break, 80°C | ISO 527-2 | 5.0 % | |
| Bending modulus | -40°C | ISO 178 | 11600 Mpa |
| 23°C | ISO 178 | 9500 Mpa | |
| 80°C | ISO 178 | 5800 Mpa | |
| bending strength | -40°C | ISO 178 | 325 Mpa |
| 23°C | ISO 178 | 290 Mpa | |
| 80°C | ISO 178 | 190 Mpa | |
| Compressive stress | -40°C | ISO 604 | 250 Mpa |
| 23°C | ISO 604 | 180 Mpa | |
| 80°C | ISO 604 | 110 Mpa | |
| shear strength | 23°C | ASTM D732 | 95.0 Mpa |
| Taber abraser | 1000 Cycles | ISO 9352 | 0.400 mg |
| Friction coefficient - vs. Metal | Suzuki Method | 0.15 |
| impact performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -40°C | ISO 179 | 10 kJ/m² |
| 23°C | ISO 179 | 13 kJ/m² | |
| Impact strength of simply supported beam without notch | -40°C | ISO 179 | 60 kJ/m² |
| 23°C | ISO 179 | 65 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.