Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | 邵氏 D, 15 秒 | ISO 868 | 40 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | ISO 11357-2 | -40.0 °C |
| melting temperature | | ISO 11357-3 | 158 °C |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | 内部方法 | 1.502 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | ISO 4589-2 | 19 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| squeeze out | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 65 to 75 °C |
| drying time | | | 4.0 to 6.0 hr |
| Melt Temperature | | | 210 to 230 °C |
| film | Test Condition | Test Method | Test Result |
|---|
| tensile strength | MD : 断裂 | ISO 527-3 | 32.0 Mpa |
| tensile strength | TD : 断裂 | ISO 527-3 | 34.0 Mpa |
| elongation | MD : 断裂 | ISO 527-3 | 500 % |
| elongation | TD : 断裂 | ISO 527-3 | 700 % |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 1.4 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | -- ohms |
| volume resistivity | | IEC 60093 | 1.5E+11 ohms·cm |
| dielectric strength | | IEC 60243-1 | 5.0 KV/mm |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 65 to 75 °C |
| drying time | | | 4.0 to 6.0 hr |
| Processing (melt) temperature | | | 200 to 270 °C |
| mold temperature | | | 25 to 60 °C |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 97.0 Mpa |
| tensile strength | 断裂 | ISO 527-2 | 30.0 Mpa |
| tensile strength | 50% 应变 | ISO 527-2 | 10.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | > 50 > 300 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.