Material Properties:Easy to process｜Glass fiber reinforced｜Glass fiber reinforced｜Dimensional stability performance｜Excellent mechanical properties
Application Areas:Engine parts｜Fitness equipment｜Industrial machinery
Color:--
Grade:Enhanced level

Material Certification

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result
Shrinkage rate			0.55 %
Shrinkage rate	Shrinkage rate			0.9 %

Basic performance	Test Condition	Test Method	Test Result
melt mass-flow rate		ISO 1133	31.9 g/10min
density		ISO 1183	1.36 g/cm³

Other performance	Test Condition	Test Method	Test Result
notes			SGS认证

Mechanical properties	Test Method	Test Result
Flexural modulus	ISO 178	5.2 GPa
bending strength	ISO 178	225.2 Mpa
Charpy Notched Impact Strength	ISO 179	86.9 kJ/m²
Tensile modulus	ISO 527	4.7 GPa
elongation at break	ISO 527	7.2 %
tensile strength	ISO 527	177.7 Mpa
Impact strength of cantilever beam gap	ISO 180	11.9 kJ/m²
Charpy Notched Impact Strength	ISO 179	14.4 kJ/m²

Thermal performance	Test Method	Test Result
melting temperature	ISO 3146	254-261 °C
Linear coefficient of thermal expansion	ISO 11359	1.5-2 10-5k
Heat distortion temperature	ISO 75	250 °C
UL flame retardant rating	UL 94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.