PC LEXAN™ 3412ECR-131 SABIC INNOVATIVE NANSHA
302
- Unit Price:US$ 2,847 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:124.3MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced｜enhance｜Flame retardant｜High rigidity
- Application Areas:Plastic bag｜Automotive External Parts｜Industrial applications｜Electrical appliances｜Lighting applications｜Medical supplies
- Color:--
- Grade:Halogen-free flame retardant grade
Material Certification
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO 75-2/Af | 136 °C |
| vicat | ASTM D152510 | 147 °C | |
| -- | ISO 306/B50 | 145 °C | |
| -- | ISO 306/B120 | 146 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 3E-05 cm/cm/°C |
| MD：23到80°C | ISO 11359-2 | 3E-05 cm/cm/°C | |
| TD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C | |
| TD：23to80°C | ISO 11359-2 | 7E-05 cm/cm/°C | |
| RTI Elec | UL 746 | 130 °C | |
| RTI Imp | UL 746 | 130 °C | |
| RTI Str | UL 746 | 130 °C | |
| Heat Deflection Temperature | 0.45MPa,Unannealed,64.0mmSpan | ISO 75-2/Bf | 141 °C |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 141 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| 3.0mm | UL 94 | 5VA | |
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 1.0mm | IEC 60695-2-13 | 825 °C |
| Limiting Oxygen Index | ISO 4589-2 | 40 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 40 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 110 J/m |
| 23°C | ASTM D256 | 110 J/m | |
| -30°C | ISO 180/1A | 6.0 kJ/m² | |
| 23°C | ISO 180/1A | 7.0 kJ/m² | |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 35 kJ/m² |
| 23°C | ISO 180/1U | 35 kJ/m² | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 20.0 J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 5.0 kJ/m² |
| 23°C | ISO 179/1eA | 6.0 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 40 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.30 g/cm³ | |
| ISO 1183 | 1.36 g/cm³ | ||
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 7.0 g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 7.00 cm3/10min |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.20-0.50 % |
| TD：3.20mm | 内部方法 | 0.20-0.50 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.29 % |
| 平衡,23°C,50%RH | ISO 62 | 0.12 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 50Hz | IEC 60250 | 3.30 |
| 60Hz | IEC 60250 | 3.30 | |
| 1MHz | IEC 60250 | 3.30 | |
| Dissipation Factor | 50Hz | IEC 60250 | 0.020 |
| 60Hz | IEC 60250 | 0.020 | |
| 1MHz | IEC 60250 | 0.010 | |
| arc resistance | ASTM D495 | PLC7 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 3 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 0 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 5500 Mpa | |
| ISO 527-2/1 | 6000 Mpa | ||
| tensile strength | 屈服 | ASTM D638 | 90.0 Mpa |
| 屈服 | ISO 527-2/5 | 95.0 Mpa | |
| 断裂 | ASTM D638 | 87.0 Mpa | |
| 断裂 | ISO 527-2/5 | 90.0 Mpa | |
| elongation | 屈服 | ASTM D638 | 3.1 % |
| Tensile strain | 屈服 | ISO 527-2/5 | 2.8 % |
| 断裂 | ISO 527-2/5 | 3.2 % | |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 5000 Mpa |
| ISO 178 | 5500 Mpa | ||
| bending strength | ISO 178 | 140 Mpa | |
| 屈服,50.0mm跨距 | ASTM D790 | 156 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.