Material Description
- Material Properties:Flame retardant｜High rigidity｜Bromine free｜Filler: Mineral filler｜filler｜Mineral filler｜filler｜30%｜Filler is rigid by weight｜High bromine free flame retardancy
- Application Areas:Industrial applications｜Business equipment｜Business equipment｜Industrial applications｜Business equipment｜Industrial applications｜Industrial applications｜Business equipment
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 120 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 108 °C | |
| vicat | ISO 306/B50 | 122 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 3.2E-05 cm/cm/°C |
| TD | ISO 11359-2 | 3.7E-05 cm/cm/°C | |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 120 ℃ |
| 热变形温度，1.80MPa,未退火 | ISO 75-2/A | 108 ℃ | |
| 维卡软化温度 | ISO 306/B50 | 122 ℃ | |
| 线形热膨胀系数，流动 | ISO 11359-2 | 3E-05 cm/cm/℃ | |
| 线形热膨胀系数，横向 | ISO 11359-2 | 3.5E-05 cm/cm/℃ |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | 3.0 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179 | 18 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1E+16 ohms | |
| IEC 60093 | 1E+16 ohms |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.40 g/cm³ | |
| shrinkage rate | TD:4.00mm | 内部方法 | 0.20-0.40 % |
| MD:4.00mm | 内部方法 | 0.10-0.30 % | |
| density | ISO 1183 | 1.4 g/m3 | |
| shrinkage rate | TD：4.00mm | 内部方法 | 0.2-0.4 % |
| MD：4.00mm | 内部方法 | 0.1-0.3 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 9000 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 66.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/5 | 2.0 % |
| flexural modulus | ISO 178 | 8000 Mpa | |
| bending strength | ISO 178 | 100 Mpa | |
| Tensile modulus | ISO 527-2/1 | 9000 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 66 Mpa |
| Tensile strain | 断裂 | ISO 527-2/5 | 2.0 % |
| flexural modulus | ISO 178 | 8000 Mpa | |
| bending strength | ISO 178 | 100 Mpa | |
| Charpy Notched Impact Strength | ISO 179 | 3 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179 | 18 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.