ASA GELOY™  CR7500 BK1041 SABIC INNOVATIVE US

250
  • Unit Price:US$ 2,162 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    41MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Thermal stability｜Antistatic｜High mobility
  • Application Areas:Automotive Applications｜Electrical applications
  • Color:--
  • Grade:Impact resistant grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Dart impact23°C, Total EnergyASTM D376330.0 J
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulus--2ASTM D6381970 Mpa
Tensile modulus--ISO 527-2/12040 Mpa
tensile strengthYield3ASTM D63840.0 Mpa
tensile strengthYieldISO 527-2/543.0 Mpa
tensile strengthBreak3ASTM D63833.0 Mpa
tensile strengthBreakISO 527-2/535.0 Mpa
elongationYield3ASTM D6383.6 %
elongationYieldISO 527-2/53.3 %
elongationBreak3ASTM D63860 %
elongationBreakISO 527-2/519 %
Bending modulus50.0 mm Span4ASTM D7902170 Mpa
Bending modulus--5ISO 1782060 Mpa
bending strength--5,6ISO 17864.0 Mpa
bending strengthYield, 50.0 mm Span4ASTM D79068.0 Mpa
injectionTest ConditionTest MethodTest Result
drying temperature85 to 95 °C
drying time3.0 to 4.0 hr
Suggested maximum moisture content0.040 %
Suggested injection volume40 to 80 %
Temperature at the rear of the barrel230 to 250 °C
Temperature in the middle of the barrel235 to 255 °C
Temperature at the front of the material cylinder245 to 260 °C
Spray nozzle temperature235 to 255 °C
Processing (melt) temperature255 to 270 °C
Mold temperature60 to 85 °C
Back pressure0.300 to 1.00 Mpa
Screw speed30 to 80 rpm
Exhaust hole depth0.038 to 0.076 mm
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature1.8 MPa, Unannealed, 3.20 mmASTM D64890.0 °C
Hot deformation temperature1.8 MPa, Unannealed, 4.00 mm, 100 mm Span9ISO 75-2/Ae88.0 °C
Hot deformation temperature1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8ISO 75-2/Af89.0 °C
Vicat softening temperature--ASTM D15251098.0 °C
Vicat softening temperature--ISO 306/B50102 °C
Vicat softening temperature--ISO 306/B120105 °C
Ball Pressure Test98°CIEC 60695-10-2通过
Linear coefficient of thermal expansionFlow : -40 to 40°CASTM E8318.4E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40 to 40°CASTM E8319.5E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40°CISO 11359-29.5E-5 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
melt mass-flow rate220°C/10.0 kgASTM D12386.3 g/10 min
melt mass-flow rate260°C/5.0 kgASTM D123811 g/10 min
Melt Volume Flow Rate (MVR)220°C/10.0 kgISO 11336.00 cm3/10min
Melt Volume Flow Rate (MVR)260°C/5.0 kgISO 113310.0 cm3/10min
Shrinkage rate3.20 mm，FlowInternal Method0.50 - 0.80 %
Water absorption rateSaturation, 23°CISO 620.50 %
Water absorption rateEquilibrium, 23°C, 50% RHISO 620.20 %
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.