PC LEXAN™ ML7647-BK1D0080 SABIC EU

297

Unit Price:US$ 4,462 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
15.1MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High impact resistance｜Fatigue resistance｜Middle flow
Application Areas:Fitness equipment｜Household appliances｜Electronic field｜Electrical field
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C, Total Energy	ASTM D3763	69.0 J

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Yield, 50.0 mm Span4	ASTM D790	87.0 Mpa
bending strength	bending strength	--5,6	ISO 178	86.0 Mpa
tensile strength	Break	ISO 527-2/50	50.0 Mpa
	tensile strength	Break3	ASTM D638	54.0 Mpa
		tensile strength	Yield	ISO 527-2/50	52.0 Mpa
		tensile strength	tensile strength	Yield3	ASTM D638	52.0 Mpa
Tensile modulus	--	ISO 527-2/1	2150 Mpa
Tensile modulus	Tensile modulus	--2	ASTM D638	2180 Mpa
Bending modulus	--5	ISO 178	2160 Mpa
Bending modulus	Bending modulus	50.0 mm Span4	ASTM D790	2130 Mpa
elongation	Break	ISO 527-2/50	94 %
	elongation	Break3	ASTM D638	100 %
		elongation	Yield	ISO 527-2/50	5.3 %
		elongation	elongation	Yield3	ASTM D638	5.0 %

injection	Test Condition	Test Method	Test Result
drying temperature			120 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			40 to 60 %
Temperature at the rear of the barrel			270 to 295 °C
Temperature in the middle of the barrel			280 to 305 °C
Temperature at the front of the material cylinder			295 to 315 °C
Spray nozzle temperature			290 to 310 °C
Processing (melt) temperature			295 to 315 °C
Mold temperature			70 to 95 °C
Back pressure			0.300 to 0.700 Mpa
Screw speed			40 to 70 rpm
Exhaust hole depth			0.025 to 0.076 mm

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ISO 11359-2	7.1E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	7.2E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	7.5E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	6.9E-5 cm/cm/°C
Vicat softening temperature		ASTM D15259	138 °C
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8	ISO 75-2/Af	119 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	118 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.15 %
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	0.26 %
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.80 %
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	11.0 cm3/10min
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	12 g/10 min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC LEXAN™ ML7647-BK1D0080 SABIC EU

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet