PEI ULTEM™ 2300-1001 SABIC INNOVATIVE US
194
- Unit Price:US$ 7,779 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced｜Flame retardant｜enhance
- Application Areas:Automotive Applications｜Fitness equipment
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 114 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| RTI Elec | UL 746 | 180 °C | |
| RTI Imp | UL 746 | 170 °C | |
| RTI Str | UL 746 | 180 °C | |
| Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTM D648 | 212 °C |
| 1.8MPa,未退火,6.40mm | ASTM D648 | 210 °C | |
| vicat | ASTM D15255 | 228 °C | |
| Linear coefficient of thermal expansion | MD：-20to150°C | ASTME831 | 2E-05 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.25mm | UL 94 | V-0 |
| 1.2mm | UL 94 | 5VA | |
| Limiting Oxygen Index | ASTM D2863 | 50 % | |
| NBSSmokeDensity-Flaming,Ds,4min | ASTME662 | 1.60 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 85 J/m |
| 23°C | ASTM D4812 | 430 J/m | |
| 3.20mm | ASTM D256 | 490 J/m |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.51 g/cm³ | |
| melt mass-flow rate | 337°C/6.6kg | ASTM D1238 | 5.0 g/10min |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.20-0.40 % |
| TD：3.20mm | 内部方法 | 0.20-0.40 % | |
| Water absorption rate | 24hr | ASTM D570 | 0.16 % |
| 平衡,23°C | ASTM D570 | 0.90 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | ASTM D257 | 3E+16 ohms·cm | |
| dielectric strength | 1.60mm,inAir | ASTM D149 | 25 KV/mm |
| 1.60mm,在油中 | ASTM D149 | 30 KV/mm | |
| dielectric constant | 1kHz | ASTM D150 | 3.70 |
| Dissipation Factor | 1kHz | ASTM D150 | 1.5E-03 |
| 2.45GHz | ASTM D150 | 5.3E-03 | |
| arc resistance | ASTM D495 | PLC6 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 4 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 4 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 1 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 9310 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 169 Mpa |
| 断裂 | ASTM D638 | 159 Mpa | |
| elongation | 断裂 | ASTM D638 | 3.0 % |
| flexural modulus | 100mmSpan | ASTM D790 | 8960 Mpa |
| bending strength | Break,100mmSpan | ASTM D790 | 228 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.