PPO NORYL™ N1150-BK1066 SABIC INNOVATIVE SHANGHAI

269

Unit Price:US$ 4,167 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Conductive｜Glass fiber reinforced
Application Areas:electromagnetic shielding
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	4.0 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	6.0 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	40.0 J
Impact strength of cantilever beam gap	23°C	ISO 180/1A	6.0 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.75mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	2700 Mpa
bending strength	Yield,50.0mmSpan	ASTM D790	117 Mpa
bending strength	bending strength		ISO 178	105 Mpa
Bending modulus		ISO 178	2600 Mpa
Bending modulus	Bending modulus	50.0mmSpan	ASTM D790	3050 Mpa
Tensile strain	Break	ISO 527-2/50	7.0 %
elongation	Break	ASTM D638	8.0 %
Tensile modulus		ISO 527-2/1	2650 Mpa
tensile strength	Yield	ASTM D638	75.0 Mpa
	tensile strength	Yield	ISO 527-2/50	72.0 Mpa
		tensile strength	Break	ASTM D638	55.0 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	52.0 Mpa
elongation	Yield	ASTM D638	4.0 %
Tensile strain	Yield	ISO 527-2/50	3.5 %

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	5.8E-05 cm/cm/°C
	Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	5.8E-05 cm/cm/°C
		Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	5.5E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	5.5E-05 cm/cm/°C
Vicat softening temperature	--	ISO 306/B120	132 °C
	Vicat softening temperature	--	ISO 306/B50	130 °C
	Vicat softening temperature	Vicat softening temperature		ASTM D152510	130 °C
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	109 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	108 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Saturation,23°C	ISO 62	0.070 %
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70 %
Melt Volume Flow Rate (MVR)	280°C/5.0kg	ISO 1133	15.0 cm3/10min
melt mass-flow rate	280°C/5.0kg	ASTM D1238	15 g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PPO NORYL™ N1150-BK1066 SABIC INNOVATIVE SHANGHAI

Material Description

Technical Data Sheet Compare

Technical Data Sheet