PPO/PA

PPO/PA NORYL GTX™ GTX8410-1710 SABIC INNOVATIVE US

371

Unit Price:US$ 3,992 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
65MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility｜dimensional stability ｜High temperature resistance｜Hydrolysis resistance｜Filler: Glass fiber reinforced material｜40% filler by weight
Application Areas:Electrical applications｜Industrial machinery｜Parts under the hood of a car
Color:--
Grade:Injection grade

Technical Data Sheet

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	--2	ASTM D638	13500 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	13900 Mpa
tensile strength	Break3	ASTM D638	178 Mpa
tensile strength	tensile strength	Break	ISO 527-2/5	198 Mpa
elongation	Break3	ASTM D638	2.0 %
elongation	elongation	Break	ISO 527-2/5	2.0 %
Bending modulus	50.0mmSpan4	ASTM D790	11900 Mpa
Bending modulus	Bending modulus	--5	ISO 178	12300 Mpa
bending strength	--5,6	ISO 178	280 Mpa
bending strength	bending strength	Yield,50.0mmSpan4	ASTM D790	249 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	1.6E-5到2.0E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	9.0E-5到9.4E-5 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	260 °C
	Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan9	ISO 75-2/Bf	258 °C
		Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	247 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan9	ISO 75-2/Af	244 °C
Vicat softening temperature		ISO 306/B50	246 °C

Physical properties	Test Condition	Test Method	Test Result
Melt Volume Flow Rate (MVR)	220°C/5.0kg	ISO 1133	10.0 cm3/10min
Shrinkage rate	MD:3.20mm	Internal Method	0.24-0.27 %
Shrinkage rate	Shrinkage rate	TD:3.20mm	Internal Method	0.60-0.63 %
Water absorption rate	Equilibrium,23°C	ASTM D570	0.30 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.10 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	108

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PPO/PA NORYL GTX™ GTX8410-1710 SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet