Material Description
- Material Properties:Chemical resistance｜High mobility｜Glass fiber reinforced｜High impact resistance
- Application Areas:Automotive External Parts
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 125 °C |
| 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 116 °C | |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距7 | ISO 75-2/Af | 101 °C | |
| vicat | -- | ASTM D15258 | 121 °C |
| -- | ISO 306/B50 | 135 °C | |
| -- | ISO 306/B120 | 130 °C | |
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 3.9E-5 cm/cm/°C |
| 横向 : -40 到 40°C | ASTM E831 | 7.6E-5 cm/cm/°C | |
| 横向 : -40°C | ISO 11359-2 | 7.6E-5 cm/cm/°C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | -30°C, Energy at Peak | ASTM D3763 | 3.00 J |
| -30°C, Total Energy | ASTM D3763 | 3.00 J | |
| -20°C, Energy at Peak | ASTM D3763 | 4.00 J | |
| 23°C, Total Energy | ASTM D3763 | 8.00 J |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 250°C/5.0 kg | ASTM D1238 | 15 g/10 min |
| Melt volume flow rate | 265°C/5.0 kg | ISO 1133 | 27.0 cm3/10min |
| shrinkage rate | 流动 : 3.20 mm | 内部方法 | 0.40 - 0.60 % |
| 横向流动 : 3.20 mm | 内部方法 | 0.40 - 0.60 % | |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.50 % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.15 % |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 110 °C | ||
| drying time | 4.0 to 6.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 50 to 80 % | ||
| Temperature at the rear of the barrel | 250 to 270 °C | ||
| Temperature in the middle of the barrel | 255 to 275 °C | ||
| Temperature at the front of the material cylinder | 260 to 280 °C | ||
| Spray nozzle temperature | 255 to 275 °C | ||
| Processing (melt) temperature | 260 to 280 °C | ||
| mold temperature | 65 to 95 °C | ||
| Back pressure | 0.300 to 0.600 Mpa | ||
| screw speed | 50 to 80 rpm | ||
| Exhaust hole depth | 0.013 to 0.020 mm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | --1 | ASTM D638 | 5310 Mpa |
| -- | ISO 527-2/1 | 4800 Mpa | |
| tensile strength | 屈服2 | ASTM D638 | 84.0 Mpa |
| 屈服 | ISO 527-2/5 | 84.0 Mpa | |
| 断裂2 | ASTM D638 | 84.0 Mpa | |
| 断裂 | ISO 527-2/5 | 84.0 Mpa | |
| elongation | 屈服2 | ASTM D638 | 3.0 % |
| 屈服 | ISO 527-2/5 | 3.0 % | |
| 断裂2 | ASTM D638 | 3.0 % | |
| 断裂 | ISO 527-2/5 | 3.0 % | |
| flexural modulus | 50.0 mm 跨距3 | ASTM D790 | 3910 Mpa |
| --4 | ISO 178 | 4010 Mpa | |
| bending strength | --4,5 | ISO 178 | 133 Mpa |
| 屈服, 50.0 mm 跨距3 | ASTM D790 | 131 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.