PC LEXAN™ HFD4271 BK1G100L SABIC INNOVATIVE NANSHA
163
- Unit Price:US$ 5,644 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility｜Hydrolysis resistance
- Application Areas:Electrical applications｜Automotive Applications｜Mechanical accessories
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 131 °C |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 125 °C | |
| vicat | ISO 306/B120 | 135 °C | |
| ball-indentation hardness | 123 到 127°C | IEC 60695-10-2 | 通过 |
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 4.0E-5 cm/cm/°C |
| 流动 : 23 到 80°C | ISO 11359-2 | 3.0E-5 cm/cm/°C | |
| 横向 : -40 到 40°C | ASTM E831 | 7.0E-5 cm/cm/°C | |
| 横向 : 23 到 80°C | ISO 11359-2 | 8.0E-5 cm/cm/°C | |
| RTI Elec | UL 746 | 80.0 °C | |
| RTI Imp | UL 746 | 80.0 °C | |
| RTI | UL 746 | 80.0 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.40 mm | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 9.0 kJ/m² |
| 23°C | ISO 179/1eA | 18 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 100 kJ/m² |
| 23°C | ISO 179/1eU | 110 kJ/m² | |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 1700 J/m |
| -30°C6 | ISO 180/1U | 68 kJ/m² | |
| 23°C6 | ISO 180/1U | 93 kJ/m² | |
| Dart impact | 23°C, Total Energy | ASTM D3763 | 36.0 J |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 15 g/10 min |
| Melt volume flow rate | 300°C/1.2 kg | ISO 1133 | 14.0 cm3/10min |
| shrinkage rate | 流动 : 3.20 mm | 内部方法 | 0.20 - 0.30 % |
| 横向流动 : 3.20 mm | 内部方法 | 0.40 - 0.50 % | |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.13 % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.040 % |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 120 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 40 to 60 % | ||
| Temperature at the rear of the barrel | 265 to 290 °C | ||
| Temperature in the middle of the barrel | 275 to 300 °C | ||
| Temperature at the front of the material cylinder | 290 to 310 °C | ||
| Spray nozzle temperature | 280 to 305 °C | ||
| Processing (melt) temperature | 290 to 310 °C | ||
| mold temperature | 70 to 95 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| screw speed | 40 to 70 rpm | ||
| Exhaust hole depth | 0.025 to 0.076 mm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 3700 Mpa | |
| tensile strength | 屈服3 | ASTM D638 | 53.0 Mpa |
| 屈服 | ISO 527-2/5 | 59.0 Mpa | |
| 断裂3 | ASTM D638 | 39.0 Mpa | |
| 断裂 | ISO 527-2/5 | 48.0 Mpa | |
| elongation | 屈服3 | ASTM D638 | 3.0 % |
| 屈服 | ISO 527-2/5 | 3.0 % | |
| 断裂 | ISO 527-2/5 | 9.0 % | |
| flexural modulus | 50.0 mm 跨距 | ASTM D790 | 3300 Mpa |
| bending strength | 屈服, 50.0 mm 跨距 | ASTM D790 | 95.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.