Material Description

Material Properties:Thermal stability｜High temperature resistance
Application Areas:Electronic and Electrical Applications｜Automotive components｜Engine parts
Color:--
Grade:Enhanced level

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Multi axis Instrumented Impact Energy		ISO 6603-2	34.1 J
Dart impact	23°C,EnergyatPeakLoad	ASTM D3763	30.6 J
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	140 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	29 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Break	ASTM D638	47.6 Mpa
tensile strength	tensile strength	Break	ISO 527-2	50.0 Mpa
elongation	Yield	ASTM D638	6.1 %
tensile strength	Yield	ISO 527-2	53.0 Mpa
tensile strength	tensile strength	Yield	ASTM D638	51.7 Mpa
Tensile modulus		ISO 527-2/1	2200 Mpa
Tensile modulus	Tensile modulus		ASTM D638	2070 Mpa
Wear factor	Washer	ASTM D3702Modified	60.0 10^-10in^5-min/ft-lb-hr
Friction coefficient	Static	ASTM D3702Modified	0.070
Friction coefficient	Friction coefficient	Dynamic	ASTM D3702Modified	0.18
bending strength		ISO 178	84.1 Mpa
bending strength	bending strength		ASTM D790	80.3 Mpa
Bending modulus		ISO 178	2400 Mpa
Bending modulus	Bending modulus		ASTM D790	2190 Mpa
elongation	Break	ASTM D638	38 %
Tensile strain	Yield	ISO 527-2	5.5 %

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	131 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	128 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.15 %
Water absorption rate	Water absorption rate	24hr,50%RH	ASTM D570	0.12 %
Shrinkage rate	MD:24hr	ISO 294-4	0.83 %
	Shrinkage rate	TD:24hr	ISO 294-4	0.88 %
	Shrinkage rate	Shrinkage rate	MD：24hr	ASTM D955	0.80-0.90 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.