PPO

PPO NORYL™ EXNL1355-701S SABIC INNOVATIVE SHANGHAI

206

Unit Price:US$ 4,043 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High temperature resistance｜Hydrolysis resistance｜wear resistant
Application Areas:Instrument panel components｜Mechanical Engineering｜valve
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C,TotalEnergy	ASTM D3763	34.2 J
Impact strength of cantilever beam gap	23°C	ISO 180/1A	16 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	7.8 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	16 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Break	ISO 527-2/50	53.3 Mpa
elongation	Yield	ASTM D638	5.2 %
Tensile strain	Yield	ISO 527-2/50	4.9 %
tensile strength	Break	ASTM D638	51.3 Mpa
	tensile strength	Yield	ISO 527-2/50	64.9 Mpa
	tensile strength	tensile strength	Yield	ASTM D638	63.3 Mpa
bending strength	Yield,50.0mmSpan	ASTM D790	104 Mpa
Tensile modulus		ISO 527-2/1	2910 Mpa
Tensile modulus	Tensile modulus		ASTM D638	2170 Mpa
elongation	Break	ASTM D638	29 %
Tensile strain	Break	ISO 527-2/50	21 %
Bending modulus	50.0mmSpan	ASTM D790	2630 Mpa
Bending modulus	Bending modulus		ISO 178	2630 Mpa
bending strength		ISO 178	107 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	7.4E-05 cm/cm/°C
	Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	7.1E-05 cm/cm/°C
		Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	7.1E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	7.4E-05 cm/cm/°C
Vicat softening temperature	--	ISO 306/B120	138 °C
	Vicat softening temperature	--	ISO 306/B50	136 °C
	Vicat softening temperature	Vicat softening temperature		ASTM D152510	136 °C
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	116 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	115 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.80 %
Melt Volume Flow Rate (MVR)	280°C/5.0kg	ISO 1133	9.85 cm3/10min
melt mass-flow rate	280°C/5.0kg	ASTM D1238	9.6 g/10min
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.050 %
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.25 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PPO NORYL™ EXNL1355-701S SABIC INNOVATIVE SHANGHAI

Material Description

Technical Data Sheet Compare

Technical Data Sheet